Zinc oxide (ZnO) nanoparticles have shown great potential because of their versatile and promising applications in different fields, including solar cells. Various methods of synthesizing ZnO materials have been reported. In this work, controlled synthesis of ZnO nanoparticles was achieved via a simple, cost-effective, and facile synthetic method. Using transmittance spectra and film thickness of ZnO, the optical band gap energies were calculated. For as-synthesized and annealed ZnO films, the bandgap energies were found to be 3.40 eV and 3.30 eV, respectively. The nature of the optical transition indicates that the material is a direct bandgap semiconductor. Spectroscopic ellipsometry (SE) analysis was used to extract dielectric functions where the onset of optical absorption of ZnO was observed at lower photon energy due to annealing of the nanoparticle film. Similarly, X-ray diffraction (XRD) and scanning electron microscopy (SEM) data revealed that the material is pure and crystalline in nature, with the average crystallite size of ~9 nm.

Electrical transport properties [carrier concentration (N), mobility (μ), effective mass (m*), resistivity (ρ), and scattering time (τ)] are deduced from free carrier optical absorption using noncontacting optical Hall effect measurements. Here, we use this technique to determine N, μ, and m* for semiconductor absorber materials for photovoltaic (PV) devices. As case studies, PV component materials including thin-film methylammonium lead iodide, cadmium telluride, and copper indium diselenide as well as silicon wafers are characterized. Optical Hall effect measurements involve collecting long wavelength ellipsometric spectra under the application of an external magnetic field to determine N and μ for these thin films, and N, μ, and m* for the silicon wafers. ρ and τ are also determined for each sample from N, μ, and m* using the Drude model. In all cases, an additional transport parameter measurement is accessible relative to standard optical measurements alone even for the PV absorber materials having low free carrier absorption. As the technique is noncontacting, it could be very useful for the determination of transport properties of layers in complex multilayer stacks such as those in thin film and wafer-based PV devices.

Motivated by their utility in CdTe-based thin film photovoltaics (PV) devices, an investigation of thin films of the magnesium-zinc oxide (Mg_xZn_1−xO or MZO) alloy system was undertaken applying spectroscopic ellipsometry (SE). Dominant wurtzite phase MZO thin films with Mg contents in the range 0 ≤ x ≤ 0.42 were deposited on room temperature soda lime glass (SLG) substrates by magnetron co-sputtering of MgO and ZnO targets followed by annealing. The complex dielectric functions ε of these films were determined and parameterized over the photon energy range from 0.73 to 6.5 eV using an analytical model consisting of two critical point (CP) oscillators. The CP parameters in this model are expressed as polynomial functions of the best fitting lowest CP energy or bandgap E₀ = E_g, which in turn is a quadratic function of x. As functions of x, both the lowest energy CP broadening and the Urbach parameter show minima for x ~ 0.3, which corresponds to a bandgap of 3.65 eV. As a result, it is concluded that for this composition and bandgap, the MZO exhibits either a minimum concentration of defects in the bulk of the crystallites or a maximum in the grain size, an observation consistent with measured X-ray diffraction line broadenings. The parametric expression for ε developed here is expected to be useful in future mapping and through-the-glass SE analyses of partial and complete PV device structures incorporating MZO.

Copper indium gallium diselenide, Cu(In,Ga)Se2, thin-film of about 1.2 μm has been deposited on Mo coated soda lime glass by thermal co-evaporation of Cu, In, Ga, and Se sources. The thin film CIGS was characterized by energy dispersive spectroscopy (EDS) and identified the elemental composition of Cu, In, Ga and Se in the film. A CIGS device was completed by the successive deposition of multiple layers; SLG/Mo/CIGS/CdS/ZnO/ITO which yielded the efficiency of 11%. External spectroscopic ellipsometry (ex-situ SE) was performed on the completed device and the device analysis was performed. Starting with the parameterized complex dielectric functions of the individual component layers, SE analysis was performed using a step-wise procedure that ranks the fitting parameters according to their ability to reduce the mean square error (MSE) of the fit. The resulting layer thicknesses and dielectric functions were used to simulate the external quantum efficiency (EQE) of the device assuming complete active layer collection. Electronic losses were identified by comparison of simulated EQE with the measured EQE. The ultimate goal of this work is the optimization of narrow band-gap CIGS-related solar cells for the bottom layer in tandem devices.