With the rapid advancement of 3D-printing technology, additive manufacturing using FDM extrusion has emerged as a prominent method in manufacturing. However, it encounters certain limitations, notably in surface quality and dimensional accuracy. Addressing issues related to stability and surface roughness necessitates the integration of 3D-printing technology with traditional machining, a strategy known as the hybrid technique. This paper presents a study of the surface geometric parameters and microstructure of plastic parts produced by FDM. Sleeve-shaped samples were 3D-printed from polyethylene terephthalate glycol material using variable layer heights of 0.1 mm and 0.2 mm and then subjected to the turning process with PVD-coated DCMT11T304 turning inserts using variable cutting parameters. The cutting depth was constant at 0.82 mm. Surface roughness values were correlated with the cutting tool feed rate and the printing layer height applied. The selected specimen’s microstructure was studied with a Zeiss EVO MA 15 scanning electron microscope. The roundness was measured with a Keyence VR-6200 3D optical profilometer. The research results confirmed that the additional application of turning, combined with a reduction in the feed rate (0.0506 mm/rev) and the height of the printed layer (0.1 mm), reduced the surface roughness of the sleeve (Ra = 1.94 μm) and increased its geometric accuracy.

The prerequisite of the weld bead finishing is intricately linked to the quality of the welded joint. It constitutes the final, yet pivotal, stage in its formation, significantly influencing the reliability of structural components and machines. This article delineates an innovative post-weld surface finishing method, distinguished by the movement of a specialized cutting tool along a butt weld. This method stands out due to its singular approach to machining allowance, wherein the weld bead height is considered and eradicated in a single pass of the cutting tool. Test samples were made of AISI 304L, AISI 316L stainless steels and EN AW-5058 H321, EN AW-7075 T651 aluminum alloys butt-welded with TIG methods. Following the welding process, the weld bead was finished in accordance with the innovative method to flush the bead and the base metal’s surface. For the quality control of welded joints before and after the weld finishing, two non-destructive testing methods were chosen: Penetrant Testing (PT) and Radiographic Testing (RT). This article provides results from the examination of 2D profile parameters and 3D stereometric characteristics of surface roughness using the optical method. Additionally, metallographic results are presented to assess changes in the microstructure, the microhardness, and the degree of hardening within the surface layer induced by the application of the innovative post-weld finishing method.

Hybrid machining has considerable potential for industrial applications. The process allows the limitations of additive manufacturing to be reduced and high-precision components to be produced. This article discusses tests determining the impact of 3D printing parameters, machining parameters, and selected milling tools on achieving defined surface roughness values in parts made of PETG (polyethylene terephthalate glycol). Perpendicular-shaped samples were printed by fused deposition modelling (FDM) using variable layer heights of 0.1 mm and 0.2 mm and variable feed rates of 90, 100, 110, and 120 mm/s. Surface roughness values, topography, and Abbott–Firestone curves were determined using a Keyence VR-6000 profilometer. Straight grooves were machined in the test samples using a DMG MORI CMX 600V milling machine with a rotary burr, single-edge spiral burr cutter and spiral endmill. The microstructure was examined using a Motic inverted microscope. The surface roughness parameters of the grooves were investigated. The results confirmed that the use of hybrid machining (with a printed layer height L_h = 0.1 mm, V_feed = 120 mm/s, and a cutter–rotary burr) allows for lower surface roughness parameters, i.e., Ra = 1.54 μm. The relationships developed between printing, cutting, and milling tool parameters can be employed to predict the roughness parameters of filaments with similar characteristics.