Due to the low price and good comprehensive properties, FRP composite material has become a new type of civil application material in recent years. In this paper, Araldite^® 2012 adhesive was used to bond basalt-fiber-reinforced polymer (BFRP), and the durability of its bonded joints was investigated. Experiments were carried out at 80 °C/DI water (deionized water), 80 °C/3.5% NaCl solution (3.5% SS), and 80 °C/5.0% NaCl solution (5.0% SS) at 0- (unaged), 10-, 20-, and 30-day aging. The specimen and BFRP in the environment of 80 °C/DI water, 80 °C/3.5% SS, and 80 °C/5.0% SS found salt solution under the condition of all sample water absorption decreases, and the activity of salt solution chemistry was weaker compared with deionized water. The load–displacement curve of the joint failure was obtained through quasi-static tensile experiments, and it was found that the adhesive would undergo a post-curing reaction that had a positive impact on the stiffness of the joint in a high-temperature environment. At the same time, it was found that the joint failure strength decreased less in the salt solution environment, and deionized water was more destructive than the salt solution. Referring to the change in water absorption, it was found that the change in the mechanical properties of the joint was mainly related to the permeation effect of the polymer. The change in the T_g of adhesive was measured by differential scanning calorimetry (DSC). It was found that T_g would decrease after aging, and the change in T_g was mainly related to the mobility of the molecular chain. Thermogravimetric analysis (TGA) was used to analyze the thermal behavior of the epoxy resin and some organic matter, and the main weight loss stage was 340–450 °C, which was the complete degradation of epoxy resin and some organic matter. Macro visual and microscopic scanning electron microscope (SEM) and energy dispersive X-ray spectroscopy (EDX) were used to analyze the failure section, and it can be concluded that the failure mode of joint tear failure transitioned to cohesion in the late–mixed interface failure, at the visible interface between the fiber and the resin matrix.

Fiber-reinforced polymer (FRP) materials are increasingly used in automotive industrial fields to achieve lightweight. In order to study the influence of high temperature and high humidity on the bonding structure between different materials, this paper selects basalt fiber-reinforced resin composite materials (BFRP) and aluminum alloy (Al), and uses Araldite® 2012 and Araldite® 2014, two adhesives, to make single lap joints (SLJs). The aging test was carried out for 0 (unaged), 10, 20, and 30 days under the environment of 80 °C/95% relative humidity (RH) and 80 °C/pure water. In this work, simple Fickian law was used to simulate the hygroscopic change law of dumbbell specimens of two adhesives and BFRP in a pure water environment. It was discovered that Araldite® 2012 is most affected by moisture, but the time to reach the maximum water absorption in Araldite® 2014 was shorter than in Araldite® 2012. The failure strength of the joint was obtained through a quasi-static tensile experiment, and it was found that the Araldite® 2014 adhesive joint first increased and then decreased in a high temperature environment. The strength increased by 11.63% after 20 days of aging under an 80 °C/95%RH environment, and increased by 16.66% after 10 days of aging under an 80 °C/pure water environment, which indicates that post-curing reaction occurred. The strength of Araldite® 2012 joints showed a downward trend. After 30 days of aging, it reduced by 40.38% under an 80 °C/95%RH environment and 41.11% under an 80 °C/pure water environment. By observing the load-displacement curve, it was found that, as time increased, the slope of the curve decreased, indicating that the stiffness of the bonded joint decreased with time. The failure modes of the joints were analyzed by macroscopic images and microscopic SEM methods, and the results showed that the surface failure transitions from a mixed failure to a complete tear failure over time. The failure of the basalt fiber/resin interface was because the interaction between the epoxy resin in the adhesive and the epoxy resin in BFRP was greater than the force between the basalt fiber layer and the epoxy resin layer in the BFRP sheet.