In the present research, nanocomposite antibacterial cellulose fibers of Lyocell type modified with nanosilver particles and nanosilica were obtained. Nanosilver particles were generated by the chemical reduction of silver nitrate (AgNO₃) in 50% water solution of N-methylmorpholine N-oxide (NMMO), which was applied as a direct cellulose solvent for the production of Lyocell fibers. The main aim of this study has been to obtain antibacterial cellulose fibers modified with silver nanoparticles, which are entirely safe for contact with human tissue. Taking into account the potential medical applications of the obtained fibers, the antibacterial activity and cytotoxicity of silver nanoparticles enclosed in fibers were examined in human and mouse cells. Considering the size of the silver nanoparticles with nanosilica in NMMO and their physical properties, the time of generation was the subject of a thorough analysis. The basic physical properties of the nanoparticles introduced in the fibers were tested using the UV/VIS, DLS and TEM methods. The basic properties of the fibers, namely the mechanical and hydrophilic ones, and the average degree of polymerisation of the cellulose fibers were estimated. The conditions of the synthesis of nanoparticles in NMMO with nanosilica were optimised. The results have confirmed that fibers with high-quality antibacterial properties, safe for human tissue and suitable for medical purposes, could be obtained.

The main aim of the presented research is to determine the optimal conditions for the production of silver nanoparticles (AgNPs) in N-methylmorpholine-N-oxide (NMMO), which will potentially allow to obtain small nanoparticles with uniform diameter distribution. In this paper, NMMO is used in the fibre production process, both as a direct cellulose solvent and as an Ag+ reducing system. From an industrial point of view, this method is very promising because it allows to reduce the amount of used chemicals. The UV/Vis, DLS and TEM analysis proved that the synthesis temperature and time could play a key role in nanoparticle growth control in NMMO. It was found that the optimal conditions for AgNPs synthesis are 100 °C and 0.33 h. The estimations of the antibacterial activity of the fibres were completed. The applied AgNPs synthesis conditions allow to obtain antibacterial fibres with a wide range of applications, mainly in medicine.

The main aim of the presented research was to obtain antibacterial fibers containing nanosilica with immobilized silver nanoparticles. The nanomodifier in an amount of 250 ppm, 500 ppm, 1,000 ppm, and 2,000 ppm were introduced into the cellulose fiber matrix during the cellulose dissolution process. In order to assess the influence of the nanomodifier's amount in the fiber on the antibacterial activity of modified fiber, a quantitative test of the antibacterial activity of the fibers was performed. The basic parameters of modified fibers, such as the mechanical and hygroscopic, were estimated. The size and shape of the nanomodifier in the selected fibers, as well as microanalysis of the polymer matrix, were examined. The investigations were conducted by Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), and Energy Dispersive Spectrometry (EDS). The obtained results allowed the selection of optimal fibers with strong antibacterial properties that can be potentially used for personal protection or medical purposes.