Glycine phases formed when aqueous solutions were frozen and subsequently heated under different conditions were studied by Raman scattering, x-ray diffraction, and differential scanning calorimetry (DSC) techniques. Crystallization of ice I_h was observed in all the cases. On cooling at the rates of 0.5 K/min and 5 K/min, glassy glycine was formed as an intermediate phase which lived about 1 min or less only, and then transformed into β-polymorph of glycine. Quench cooling of glycine solutions (15% w/w) in liquid nitrogen resulted in the formation of a mixture of crystalline water ice I_h and a glassy glycine, which could be preserved at cryogenic temperatures (80 K) for an indefinitely long time. This mixture remained also quite stable for some time after heating above the cryogenic temperature. Subsequent heating under various conditions resulted in the transformation of the glycine glass into an unknown crystalline phase (glycine “X-phase”) at 209–216 K, which at 218–226 K transformed into β-polymorph of glycine. The “X-phase” was characterized by Raman spectroscopy; it could be obtained in noticeable amounts using a special preparation technique and tentatively characterized by x-ray powder diffraction (P2, a = 6.648 Å, b = 25.867 Å, c = 5.610 Å, β = 113.12º); the formation of “X-phase” from the glycine glassy phase and its transformation into β-polymorph were followed by DSC. Raman scattering technique with its power for unambiguous identification of the crystalline and glassy polymorphs without limitation on the crystallite size helped us to follow the phase transformations during quenching, heating, and annealing. The experimental findings are considered in relation to the problem of control of glycine polymorphism on crystallization.

We investigated the effects of applied high pressure on thermoelectric, electric, structural, and optical properties of single-crystalline thermoelectrics, Bi₂Te₃, Bi_xSb_2−xTe₃ (x = 0.4, 0.5, 0.6), and Bi₂Te_2.73Se_0.27 with the high thermoelectric performance. We established that moderate pressure of about 2–4 GPa can greatly enhance the thermoelectric power factor of all of them. X-ray diffraction and Raman studies on Bi₂Te₃ and Bi_0.5Sb_1.5Te₃ found anomalies at similar pressures, indicating a link between crystal structure deformation and physical properties. We speculate about possible mechanisms of the power factor enhancement and suppose that pressure/stress tuning can be an effective tool for the optimization of the thermoelectric performance.