This study aims to explore the use of cellulose nanocrystals (CNC) and cellulose nanofiber (CNF), obtained from unbleached fiber of oil palm empty fruit bunches (EFB), as raw materials in fabricating aerogel, using the facile technique without solvent displacement. The CNC was isolated from sulfuric acid hydrolysis, and the CNF was fibrillated using Ultra Turrax. The CNC and CNF were mixed by ultrasonication in different ratios to produce aerogel using slow freezing (−20 °C), followed by freeze-drying. The obtained aerogel was characterized as ultralightweight and highly porous material, at the density range of 0.0227 to 0.0364 g/cm³ and porosity of 98.027 to 98.667%. Interestingly, the ratio of CNC and CNF significantly affected the characteristics of the obtained aerogel. The mixed aerogel exhibited a higher specific surface area than pure CNC or CNF, with the highest value of 202.72 m²/g for the ratio of 1:3 (CNC/CNF). In addition, the crystallinity degree of obtained aerogel showed a higher value in the range of 76.49 to 69.02%, with the highest value being obtained for higher CNC content. This study is expected to provide insight into nanocellulose-based aerogel, with a promising potential for various applications.

Pengaruh Proses Pemutihan Multi Tahap Serat Selulosa Dari Limbah Tandan Kosong Kelapa Sawit

This study investigated the effect of two-stage pretreatment using dilute H₂SO₄ followed by dilute NaOH on the physical characteristic of oil palm empty fruit bunch including crystallinity index, chemical bonding and morphology. Its effect on chemical characteristic, especially the sugar recovery have also been observed. The results showed a low crystallinity degree measured from acid-alkaline OPEFB which was confirmed by the FTIR spectra with the decrease intensity of CH₂ bending vibration at 1433 cm^-1 and crystallinity index in the amount of 57.53 %. Silica-bodies which was noticed from the raw OPEFB was successfully removed after the sequential pretreatment. High cellulose and lignin removal around 90 % and 73.1 %, respectively with a trace of acetic acid and no furfural content were achieved at the end of the pretreatment.