This preliminary study characterizes the bronze metalworking on a defensive settlement of the Lusatian culture in former Kamieniec (Chełmno land, Poland) as it is reflected through casting workshop recovered during recent excavations. Among ready products, the ones giving evidence of local metallurgy (e.g. casting moulds and main runners) were also identified. With the shrinkage cavities and dendritic microstructures revealed, the artifacts prove the implementing a casting method by the Lusatian culture metalworkers. The elemental composition indicates application of two main types of bronzes: Cu-Sn and Cu-Pb. Aside these main alloying additions, some natural impurities such as silver, arsenic, antimony and nickel were found which may be attributed to the origin of the ore and casting technology. The collection from Kamieniec was described in terms of its structure and composition. The investigations were made by means of the energy dispersive X-ray fluorescence spectroscopy (ED-XRF), scanning electron microscopy (SEM) coupled with an energy dispersive X-ray analysis system (EDS) and optical microscopy (OM). In order to fingerprint either local or non-local profile of the alloys, the ED-XRF data-set was statistically evaluated using a factor analysis (FA).

Thise research was conducted to determine the impact of the applied casting technology, mould and alloying additives on the tightness of the CuSn10 cast alloy. Under industrial conditions, a series of experimental melts were made that were characterised by varying the concentrations of the main alloying element (Sn) and the introduced alloying additives (Si, Zn, Zr). The mould was made from green sand and used the CO₂ moulding process. To assess the influence of the alloying additives, a metallographic analysis of the studied alloy was carried out, and the alloy’s microstructure was examined using optical and scanning electron microscopy. The introduced alloying additives affected the properties and microstructure of the studied alloy. As alloying additives, zirconium resulted in a visible refinement of the microstructure, while silicon improved the fluidity and quality of the casting’s external surface. The use of alloying additives and moulds made using different technologies is intended to improve the structure of the tin bronze castings produced and to find the best solution to significantly eliminate the lack of leakage of the castings. The castings were subjected to mechanical processing, and a leak test was performed using the pressure drop method. The conducted research allowed us to determine which technology, applied to production, will bring about a reduction in the problem and will inform further investigations.

One of the most interesting categories of artifacts for archaeometallurgical research includes deposits of bronze items, so-called “metallurgists hoards”. They contain, aside of final products, many fragments of raw material and, moreover, metallurgical tools. An important source for the studies on the history of metallurgical technology is hoard from Przybysław, Greater Poland district. Thus, the aim of the work is the identification and interpretation of bronze-working practices and strategies adopted by prehistoric communities of the Late Bronze Age and the Early Iron Age (ca. 600 BC). The examined objects are characterized in terms of their design, structure, and chemical composition. The methods chosen for the studies of artifacts include: metallographic macro- and microscopic observations using optical microscopy (OM) and scanning electron microscopy (SEM), the analysis of chemical composition with the methods of energy dispersive X-ray spectroscopy (EDS), and X-ray fluorescence (ED-XRF). The thermodynamic analysis of the alloys was performed on the basis of the CALPHAD method. The experimental melts allowed to verify the theoretical considerations and to determine the characteristic temperatures of changes. The old casting technology can be analyzed basing on computer modeling and computer simulation methods. Simulations in the MAGMASOFT® software are a good example to illustrate how to fill a mould cavity with a molten bronze for a hoop ornament. It is also an appropriate tool to determine temperature distribution in a mould. The simulations also show the possible disadvantages with this old technology.

As part of the studies conducted in the field of broadly understood casting of non-ferrous metals, selected results on the impact of variable additions of copper and silicon in aluminium were presented. A series of melts was carried out with copper content kept constant at a level of 2% (1st stage) and 4% (2nd stage) and variable contents of silicon introduced into aluminium. The crystallization characteristics of the examined alloys and the percentage of structural constituents at ambient temperature were obtained by modelling the thermodynamic parameters of individual phases with the CALPHAD method. The microstructure of the obtained alloys was examined and microhardness was measured by the Vickers-Hanemann method. The alloy properties were assessed based on the results of mechanical tests, including ultimate tensile strength (UTS), hardness (BHN) and elongation (E). The machinability of the tested alloys was analyzed in a machinability test carried out by the Keep-Bauer method, which consisted in drilling with a constant feed force. The obtained results clearly indicate changes in the images of microstructure, such as the reduction in grain size, solution hardening and precipitation hardening. The changes in the microstructure are also reflected in the results of mechanical properties testing, causing an increase in strength and hardness, and plasticity variations in the range of 4 ÷ 16%, mainly due to the introduced additions of copper and silicon. The process of alloy strengthening is also visible in the results of machinability tests. The plotted curves showing the depth of the hole as a function of time and the images of chips produced during the test indicate an improvement in the wear resistance obtained for the tested group of aluminium alloys with the additions of copper and silicon.

The article presents the research results obtained at the Department of Foundry of Non-Ferrous Metals at the Foundry Faculty of AGH, the University of Science and Technology, in Krakow. The research comprises the processes connected with the technology of melting, refining and making casts based on copper matrix, both contemporary and historical, especially bronzes containing tin, zinc and lead. These issues are well-known but they still pose problems for contemporary foundries. The article presents the results of modifying formulas on the improvement of mechanical properties and limiting casting defects.

In this paper, the results from studies regarding near-eutectic Al-Si alloys with Sn as an alloying addition are presented. In most Al-Si alloys, tin is regarded as a contaminant; thus, its amount is limited to up to 0.3 wt.%. The few studies that can be found in the literature regarding the behaviour of tin in aluminium alloys suggest the beneficial effect of this element on selected properties. However, these results were obtained for hypereutectic Al-Si alloys or wrought aluminium alloys. In our studies, the influence of tin contents of up to 1.7 wt.% was determined on the AlSi10 alloy. Thermal analysis, measurements of the mechanical properties of the cast and heat-treated alloy, metallographic observations (light microscopy, scanning electron microscopy), and EDS (X-ray energy dispersive spectrometry) measurement allowed us to fully describe the effect of tin on the aluminium alloy. The results of the thermal analysis showed changes in the range of the α-Al solution crystallisation and the α+β eutectic through a decrease in the alloy’s solidification start point and eutectic solidification point. As a result, the elongation of the alloy was more than double in the AlSi10Sn1.7 alloy, with an A5 value of 8.1% and a tensile strength that was above 200 MPa.