This study reports the potential of TEMPO-oxidized cellulose nanofibrils (T-CNF)/poly(vinyl alcohol) (PVA) coatings to develop functionalized membranes in the ultrafiltration regime with outstanding antifouling performance and dimensional/pH stability. PVA acts as an anchoring phase interacting with the polyethersulfone (PES) substrate and stabilizing for the hygroscopic T-CNF via crosslinking. The T-CNF/PVA coated PES membranes showed a nano-textured surface, a change in the surface charge, and improved mechanical properties compared to the original PES substrate. A low reduction (4%) in permeance was observed for the coated membranes, attributable to the nanometric coating thickness, surface charge, and hydrophilic nature of the coated layer. The coated membranes exhibited charge specific adsorption driven by electrostatic interaction combined with rejection due to size exclusion (MWCO 530 kDa that correspond to a size of ∼35–40 nm). Furthermore, a significant reduction in organic fouling and biofouling was found for T-CNF/PVA coated membranes when exposed to BSA and E. coli. The results demonstrate the potential of simple modifications using nanocellulose to manipulate the pore structure and surface chemistry of commercially available membranes without compromising on permeability and mechanical stability.

This article presents a comparative study of the surface characteristics and water purification performance of commercially available cellulose nonwoven fabrics modified, via cast coating, with different nano-dimensioned bio-based carbohydrate polymers, viz. cellulose nanocrystals (CNC), TEMPO-oxidized cellulose nanofibers (T-CNF), and chitin nanocrystals (ChNC). The surface-modified nonwoven fabrics showed an improvement in wettability, surface charge modification, and a slight decrease of maximum pore size. The modification improved the water permeance in most of the cases, enhanced the particle separation performance in a wide range of sizes, upgraded the mechanical properties in dry conditions, and showed abiotic antifouling capability against proteins. In addition, T-CNF and ChNC coatings proved to be harmful to the bacteria colonizing on the membranes. This simple surface impregnation approach based on green nanotechnology resulted in highly efficient and fully bio-based high-flux water filtration membranes based on commercially available nonwoven fabrics, with distinct performance for particle rejection, antifouling and antibacterial properties.

Considering the current trend of finding sustainable alternatives to the existing fossil-based plastics, in this review we describe what makes a bioelastomer “bio” and what this implies in terms of materials design. We analyze the current state of development of bioelastomers, including the most important types, their current and upcoming use, and their synthetic pathways. Moreover, we provide a general landscape of the hybridization or composite preparation of elastomers to acquire specific functionalities and their implementation in advanced applications, focusing mainly on electronics and biomedicine. Furthermore, we show how through the use of bioelastomers, one can, besides helping the environment, achieve materials with exceptional performances (e.g., very high mechanical properties and/or self-healing properties), which can be processed via novel techniques such as 3/4D-(bio)printing.