Microemulsion-based synthesis is found to be a versatile route to synthesize a variety of nanomaterials. The manipulation of various components involved in the formation of a microemulsion enables one to synthesize nanomaterials with varied size and shape. In this tutorial review several aspects of microemulsion based synthesis of nanocrystalline materials have been discussed which would be of interest to a cross-section of researchers working on colloids, physical chemistry, nanoscience and materials chemistry. The review focuses on the recent developments in the above area with current understanding on the various factors that control the structure and dynamics of microemulsions which can be effectively used to manipulate the size and shape of nanocrystalline materials.

Nanorods of anhydrous manganese oxalate were prepared by the reverse-micellar method using CTAB as the surfactant. Manganese oxalate precursor was used to synthesize single phase nanoparticles of various manganese oxides such as MnO, Mn₂O₃ and Mn₃O₄ under specific reaction conditions. Both MnO (28 nm) and α-Mn₂O₃ (50 nm) are stabilized as cubic phase. α-Mn₂O₃ shows a weak antiferromagnetic transition (T_N = 80 K), while the spinel Mn₃O₄ (100 nm) particles show a ferrimagnetic transition at 43 K.

Hydrogen fuel is among the cleanest renewable resources and is the best alternative to fossil fuels for the future. Hydrogen can be best produced by means of electrolysis or photoelectrolysis of water among the various routes available for hydrogen production. So far, Pt has been recognized as the best electrode material for electrochemical hydrogen production. However, the cost of the catalyst, activity, and durability make Pt-catalyzed hydrogen production unsuitable on a commercial scale. It has hence become imperative to explore low-cost, highly active and durable HER catalysts to replace platinum as a catalyst. This perspective provides key concepts and the current status of the research on the properties of nanocatalysts that influence the hydrogen evolution reaction. Important structural features controlling the surface chemistry (i.e. facets, defects, dopants), nature of supports (graphene, CNTs, black phosphorus), role of heteroatoms, media and morphology are the key points of discussion in this perspective.