This research proposed two pretreatments of viscose fabrics: oxidation with 2,2,6,6-tetramethylpiperidine-1-oxy radical (TEMPO) and coating with TEMPO-oxidized cellulose nanofibrils (TOCN), to introduce functional groups (COOH and CHO) suitable for irreversible binding of chitosan nanoparticles without and with embedded zinc (NCS and NCS + Zn, respectively) and consequently achieving washing durable antibacterial properties of the chitosan nanoparticles functionalized fabrics. The characterizations of pretreated and chitosan nanoparticles functionalized fabrics were performed by FTIR and XPS spectroscopy, elemental analysis, inductively coupled plasma optical emission spectrometry, zeta potential measurements, scanning electron microscopy, determination of COOH and CHO groups content, and antimicrobial activity under dynamic contact conditions. Influence of pretreatments on NCS and NCS + Zn adsorption, chemical, electrokinetic, and antibacterial properties as well as morphology, and washing durability of NCS and NCS + Zn functionalized fabrics were studied and compared. Washing durability was evaluated through changes in the chitosan and zinc content, zeta potential, and antibacterial activity after 1, 3, and 5 washing cycles. Pretreatments improved washing durability of antibacterial properties of chitosan nanoparticles functionalized fabrics. The NCS and NCS + Zn functionalized pretreated fabrics preserved antibacterial activity against S. aureus after five washing cycles, while antibacterial activity against E. coli was preserved only after one washing cycle in the case NCS + Zn functionalized pretreated viscose fabrics.

The main objective of this study was to obtain chitosan functionalized viscose fabric with improved antibacterial properties and washing durability. In this regard carboxyl and aldehyde groups, as binding points for irreversible chitosan attachment into/onto viscose fabric, were introduced by two different pretreatments: 2,2,6,6-tetramethylpiperidine-1-oxy radical (TEMPO) oxidation and coating with TEMPO oxidized cellulose nanofibrils (TOCN). The Fourier transform infrared spectroscopy, elemental analysis, zeta potential measurements, scanning electron microscopy, breaking strength and antibacterial testing were used to evaluate the influence of these pretreatments on chitosan binding, but also on chemical, electrokinetic, morphological, mechanical and antibacterial properties of pretreated and chitosan functionalized viscose fabrics. Washing durability of chitosan functionalized viscose was monitored through changes in the chitosan content, electrokinetic and antibacterial properties after multiple washing. TOCN coating improves mechanical properties of fabric, while TEMPO oxidation deteriorates them. The results show that both pretreatments improve chitosan adsorption and thus antibacterial properties, which are highly durable to washing. After five washings, the chitosan functionalized pretreated viscose fabrics preserve their antibacterial activity against Staphylococcus aureus, while antibacterial activity against Escherichia coli was lost. TOCN coated and chitosan functionalized viscose fabric is a high value-added product with simultaneously improved antibacterial and mechanical properties, which may find application as medical textiles.

Considering the increasing resistance of numerous bacteria to antibiotics, a novel wound dressing material was developed with naturally acquired olive leaf extract, which shows not only good antimicrobial activity, but also very good antioxidant activity. Besides that, the leaves are treated as waste in agriculture, giving an impact on waste management. An environmentally friendly procedure, electrospinning, was used for the first time to prepare polysaccharide nanofibrous mats with incorporated olive leaf extract, with the unique property of releasing the active phenolic components in a prolonged manner over 24 hours. The developed electrospun mats were characterized using scanning electron microscopy, high-performance liquid chromatography and ultraviolet-visible spectroscopy for determination of free radical scavenging activity by 2,2-diphenyl-1-picrylhydrazyl, antimicrobial testing and release kinetics. Antimicrobial tests have shown that electrospun mats with olive leaf extract achieve reduction towards the tested microorganisms: Staphylococcus aureus (G+), Escherichia coli (G-), Enterococcus faecalis (G+) and Pseudomonas aeruginosa (G-), while the high antioxidant activity of olive leaf extract was preserved during the electrospinning procedure. Release of olive leaf extract from electrospun mats was mathematically modeled, and the release kinetics evaluation indicates the appropriateness of the Korsmeyer–Peppas model for fitting the obtained results of release ability due to erosion of polysaccharide nanofiber mats.