Methods for reducing weight of structural elements are important for a sustainable society. Over the recent years ultra high strength steel (UHSS) has been a successful material for designing light and strong components. Sandwich panels are interesting structural components to further explore areas where the benefits of UHSS can be utilized. The specific properties of sandwich panels make them suitable for stiffness applications and various cores have been studied extensively. In the present work, bidirectionally corrugated UHSS cores are studied experimentally and numerically. A UHSS core is manufactured by cold rolling and bonded to the skins by welding. Stiffness is evaluated experimentally in three-point bending. The tests are virtually reproduced using the finite element method. Precise discretization of the core requires large amounts of computational power, prolonging lead times for sandwich component development, which in the present work is addressed by homogenization, using an equivalent material formulation. Input data for the equivalent models is obtained by characterizing representative volume elements of the periodic cores under periodic boundary conditions. The homogenized panel reduces the number of finite elements and thus the computational time while maintaining accuracy. Numerical results are validated and agree well with experimental testing. Important findings from experimental and simulation results show that the suggested panels provide superior specific bending stiffness as compared to solid panels. This work shows that lightweight UHSS sandwiches with excellent stiffness properties can be manufactured and modeled efficiently. The concept of manufacturing a UHSS sandwich panel expands the usability of UHSS to new areas.

Shear cutting introduces residual strains, notches and cracks, which negatively affects edge-formability. This is especially relevant for forming of high-strength sheets, where edge-cracking is a serious industrial problem. Numerical modelling of the shear cutting process can aid the understanding of the sheared edge damage and help preventing edge-cracking. However, modelling of the shear cutting process requires robust and accurate numerical tools that handle plasticity, large deformation and ductile failure. The use of conventional finite element methods (FEM) may give rise to distorted elements or loss of accuracy during re-meshing schemes, while mesh-free methods have tendencies of tensile instability or excessive computational cost. In this article, the authors propose the particle finite element method (PFEM) for modelling the shear cutting process of high-strength steel sheets, acquiring high accuracy results and overcoming the stated challenges associated with FEM. The article describe the implementation of a mixed axisymmetric formulation, with the novelty of adding a ductile damage- and failure model to account for material fracture in the shear-cutting process. The PFEM shear-cutting model was validated against experiments using varying process parameters to ensure the predictive capacity of the model. Likewise, a thorough sensitivity analysis of the numerical implementation was conducted. The results show that the PFEM model is able to predict the process forces and cut edge shapes over a wide range of cutting clearances, while efficiently handling the numerical challenges involved with large material deformation. It is thus concluded that the PFEM implementation is an accurate predictive tool for sheared edge damage assessment.

Legislation regarding greenhouse gas emissions forces automotive manufacturers to bring forth new and innovative materials and structures for weight reduction of the body-in-white. The present work evaluates a lightweight ultra high strength steel sandwich concept, with perforated cores, for energy absorption applications. Hat-profile geometries, subjected to crushing, are studied numerically to evaluate specific energy absorption for the sandwich concept and solid hat-profiles of equivalent weight. Precise discretization of the perforated core requires large computational power. In the present work, this is addressed by homogenization, replacing the perforated core with a homogeneous material with equivalent mechanical properties. Input data for the equivalent material is obtained by analyzing a representative volume element, subjected to in-plane loading and out-of-plane bending/twisting using periodic boundary conditions. The homogenized sandwich reduces the number of finite elements and thereby computational time with approximately 95%, while maintaining accuracy with respect to force–displacement response and energy absorption. It is found that specific energy absorption is increased with 8–17%, when comparing solid and sandwich hat profiles of equivalent weight, and that a weight saving of at least 6% is possible for equivalent performance.

Lightweight components are in demand from the automotive industry, due to legislation regulating greenhouse gas emissions, e.g., CO₂. Traditionally, lightweighting has been done by replacing mild steels with ultra-high strength steel. The development of micro-sandwich materials has received increasing attention due to their formability and potential for replacing steel sheets in automotive bodies. A fundamental requirement for micro-sandwich materials to gain significant market share within the automotive industry is the possibility to simulate manufacturing of components, e.g., cold forming. Thus, reliable methods for characterizing the mechanical properties of the micro-sandwich materials, and in particular their cores, are necessary. In the present work, a novel method for obtaining the out-of-plane properties of micro-sandwich cores is presented. In particular, the out-of-plane properties, i.e., transverse tension/compression and out-of-plane shear are characterized. Test tools are designed and developed for subjecting micro-sandwich specimens to the desired loading conditions and digital image correlation is used to qualitatively analyze displacement fields and fracture of the core. A variation of the response from the material tests is observed, analyzed using statistical methods, i.e., the Weibull distribution. It is found that the suggested method produces reliable and repeatable results, providing a better understanding of micro-sandwich materials. The results produced in the present work may be used as input data for constitutive models, but also for validation of numerical models.

The lightweighting of heavy-duty vehicles (HDVs) is an effective strategy to reduce fuel consumption and lower CO₂ emissions in the transport sector. The widespread application of ultra-high-strength steels (UHSSs) in HDV construction offers a viable solution, particularly for thick-walled chassis components. This study aimed to support the lightweighting of heavy vehicles by developing a methodology capturing the entire warm-forming process in the range of 430–580 °C for thick-walled UHSSs—from material characterisation, including elastoplastic and fracture properties, to downstream forming process simulations. A novel 7 mm thick UHSS grade, WARMLIGHT-980 (ultimate tensile strength (UTS) of 980 MPa), intended for warm forming was investigated at 430, 505, and 580 °C using samples of reduced thickness. The results showed that thickness reduction had minimal influence on mechanical response at elevated temperatures, enabling flexible specimen design. The thermal uniformity improved in thinner samples, enhancing testing reliability. The calibrated hardening and fracture models demonstrated strong agreement with experimental data. Validated simulations of thick-walled components confirmed the accuracy of the modelling approach. The findings support the development of reliable, temperature-dependent models for warm-forming applications and contribute to the design of lighter, more sustainable HDV components without compromising structural integrity.

The use of Advanced High Strength Steel (AHSS) allows for lightweighting of sheet steel components, with maintained structural integrity of the part. However, AHSS grades show limitations in edge crack resistance, primarily influenced by sheared edge damage introduced by the shear cutting process. Numerical modelling of the shear cutting process can aid the understanding of the sheared edge damage, thus avoiding unforeseen edge cracking in the subsequent cold forming. However, the extreme deformations of the blank during the shear cutting process are likely to cause numerical instabilities and divergence using conventional Finite Element modelling. To overcome these challenges, this work presents the use of a particle-based numerical modelling method called the Particle Finite Element Method (PFEM). PFEM accurately solves some of the challenges encountered in shear cutting with the standard Finite Element method, such as large deformation, angular distortions, generation of new boundaries and presents an efficient way of transfer historical information from the old to the new mesh, minimising the results diffusion. The present work shows prediction of cut edge morphology of AHSS using a PFEM modelling scheme, where the numerical results are verified against experiments. With these results, the authors show new possibilities to obtain accurate numerical prediction of the shear cutting process, which promotes further advances in prediction of edge damaged related to shear cutting of AHSS.