Solid polymer electrolyte (SPE) composed of semi-crystalline poly (vinylidene fluoride-hexafluoropropylene) [P(VdF-HFP)] copolymer, 1-ethyl-3-methylimidazolium bis (trifluoromethyl sulphonyl) imide [EMI-BTI] and graphene oxide (GO) was prepared and its performance evaluated. The effects of GO nano-filler were investigated in terms of enhancement in ionic conductivity along with the electrochemical properties of its electrical double layer capacitors (EDLC). The GO-doped SPE shows improvement in ionic conductivity compared to the P(VdF-HFP)-[EMI-BTI] SPE system due to the existence of the abundant oxygen-containing functional group in GO that assists in the improvement of the ion mobility in the polymer matrix. The complexation of the materials in the SPE is confirmed in X-ray diffraction (XRD) and thermogravimetric analysis (TGA) studies. The electrochemical performance of EDLC fabricated with GO-doped SPE is examined using cyclic voltammetry and charge–discharge techniques. The maximum specific capacitance obtained is 29.6 F∙g⁻¹, which is observed at a scan rate of 3 mV/s in 6 wt % GO-doped, SPE-based EDLC. It also has excellent cyclic retention as it is able keep the performance of the EDLC at 94% even after 3000 cycles. These results suggest GO doped SPE plays a significant role in energy storage application.

Nanocomposite polymer electrolyte membranes (NCPEMs) based on poly(acrylic acid)(PAA) and titania (TiO₂) are prepared by a solution casting technique. The ionic conductivity of NCPEMs increases with the weight ratio of TiO₂.The highest ionic conductivity of (8.36 ± 0.01) × 10⁻⁴ S·cm⁻¹ is obtained with addition of 6 wt % of TiO₂ at ambient temperature. The complexation between PAA, LiTFSI and TiO₂ is discussed in Attenuated total reflectance-Fourier Transform Infrared (ATR-FTIR) studies. Electrical double layer capacitors (EDLCs) are fabricated using the filler-free polymer electrolyte or the most conducting NCPEM and carbon-based electrodes. The electrochemical performances of fabricated EDLCs are studied through cyclic voltammetry (CV) and galvanostatic charge-discharge studies. EDLC comprising NCPEM shows the specific capacitance of 28.56 F·g⁻¹ (or equivalent to 29.54 mF·cm⁻²) with excellent electrochemical stability.

Poly(1-vinylpyrrolidone-co-vinyl acetate)-based quasi-solid polymer electrolytes doped with potassium iodide are prepared. The highest room temperature ionic conductivity of 1.72 mS cm⁻¹ is obtained. The dielectric studies are performed to understand the ion conduction mechanism. Fourier transform infrared study has been performed to understand complexation of the poly(1-vinylpyrrolidone-co-vinyl acetate)-based quasi-solid polymer electrolytes. The best power energy conversion efficiency (η) obtained is 2.94% with short circuit current density (J_sc) of 8.05 mA cm⁻², open circuit voltage (V_oc) of 0.58 V, and fill factor of 63% under standard light intensity of 100 mW cm⁻² irradiation. GRAPHICAL ABSTRACT