Functional and structural ceramics have become irreplaceable in countless high-tech applications. However, their inherent brittleness tremendously limits the application range and, despite extensive research efforts, particularly short cracks are hard to combat. While local plasticity carried by mobile dislocations allows desirable toughness in metals, high bond strength is widely believed to hinder dislocation-based toughening of ceramics. Here, we demonstrate the possibility to induce and engineer a dislocation microstructure in ceramics that improves the crack tip toughness even though such toughening does not occur naturally after conventional processing. With modern microscopy and simulation techniques, we reveal key ingredients for successful engineering of dislocation-based toughness at ambient temperature. For many ceramics a dislocation-based plastic zone is not impossible due to some intrinsic property (e.g. bond strength) but limited by an engineerable quantity, i.e. the dislocation density. The impact of dislocation density is demonstrated in a surface near region and suggested to be transferrable to bulk ceramics. Unexpected potential in improving mechanical performance of ceramics could be realized with novel synthesis strategies.

Field-assisted processing methods, such as spark plasma sintering and flash sintering, have considerably expanded the toolbox of ceramic engineering. Depending on the conditions, substantial electric currents may flow through the material resulting in fast heating rates due to Joule heating. Here, we focus on nonthermal effects induced by electric fields during processing of fluorite- and perovskite-based ceramics. The fundamentals of how a field can directly modify defect formation and migration in crystals are discussed. In addition, the interplay of ion transport and electrical conductivity is considered, this interplay being crucial to understanding nonthermal effects caused by electric fields (as in memristive switching). Electrochemical reactions leading to new phases or reduction are also described, as are densification rates and sintering parameters that are significantly affected even though the sample temperature is held constant. Finally, as grain-boundary properties and segregation are changed by ion transport, we describe how both retardation and acceleration of grain growth can be achieved including graded microstructures.