Starch-based pH-sensing films with bacterial nanocellulose (BNC) and red cabbage anthocyanins (RCA) as active components were investigated in this research. Their structural, physical, surface and colorimetric properties were analyzed, mainly as a function of BNC concentration. The aim of the research was to relate the changes in the intermolecular interactions between the components of the films (starch, anthocyanins and BNC) to the physical, surface and colorimetric properties that are important for the primary intended application of the produced films as pH indicators in smart packaging. The results showed that maize starch (MS) was more suitable as a matrix for the stabilization of anthocyanins compared to potato starch (PS). PS-based films showed a lower value of water contact angle than MS-based films, indicating stronger hydrophilicity. The swelling behavior results indicate that the concentrations of BNC in MS-based films (cca 10%) and the concentration of about 50% BNC in PS-based films are required if satisfactory properties of the indicator in terms of stability in a wet environment are to be achieved. The surface free energy results of PS-based films with BNC were between 62 and 68 mJ/m² and with BNC and RCA between 64 and 68 mJ/m²; for MS-based films, the value was about 65 mJ/m² for all samples with BNC and about 68 mJ/m² for all samples with BNC and RCA. The visual color changes after immersion in different buffer solutions (pH 2.0–10.5) showed a gradual transition from red/pink to purple, blue and green for the observed samples. Films immersed in different buffers showed lower values of 2 to 10 lightness points (CIE L*) for PS-based films and 10 to 30 lightness points for MS-based films after the addition of BNC. The results of this research can make an important contribution to defining the influence of intermolecular interactions and structural changes on the physical, surface and colorimetric properties of bio-based pH indicators used in smart packaging applications.

The aim of this research was to analyze the influence of the solvents commonly used in flexography on photopolymer and ethylene propylene diene monomer (EPDM) flexographic printing plates and prints. EPDM plates are recommended when the reproduction process includes a higher amount of the solvents or aggressive solvents. Since additional UV treatment of flexographic printing plates could decrease the interaction between the plate and solvent, photopolymer and EPDM plates were treated with varied UV radiation and exposed to different types of solvents. Effects of the UV treatment and of the solvents on printing plate properties and on prints were analyzed. Results show that EPDM plates are more resistant to solvents in terms of the degree of swelling; however, surface properties of the plates were affected for both plate materials. In addition, the degree of swelling and increased hardness due to UV radiation were crucial for changes of the width of printed lines, and altered surface free energy affected the thickness of deposited ink film for both plate materials. Therefore, depending on the qualitative requirements of specific printed film, the duration of UV treatment can be adjusted for use with specific types of printing plate and solvent.

Thermochromic liquid crystal materials are commonly used in printing inks, opening up a wide range of possible applications. In order to ensure and control the most accurate application, the occurrence of the so-called colour play effect, i.e., the appearance of iridescent (rainbow) colours as a function of temperature, must be determined precisely. For this purpose, the temperature-dependent reflection of a sample must be measured using a spectrometer with an integrating sphere. The same values should be obtained for each sample containing the same thermochromic liquid crystalline material, irrespective of the spectrometer used, integrating sphere, layer thickness and the surface properties of the substrate. To describe this intrinsic property of the thermochromic liquid crystal material, the term communication mechanism might be considered. The research has shown how this mechanism is obtained experimentally.

In the present research, properties and performance of special effect printing inks were observed with the aim of obtaining a printed product with dual functional properties. Thermochromic liquid crystal-based printing ink (TLC) and UV-visible (daylight invisible) fluorescent inks (UVF), pure and as hybrid ink systems, were printed using a screen-printing technique on two types of uncoated paper substrates. Characterization of the paper substrates was performed, as well as detailed analysis of printed layers. Thickness, surface roughness, surface free energy, and adhesion parameters of printed layers were analysed. Spectral reflectance of pure UVF and TLC printing inks, as well as the spectral reflectance of the proposed hybrid ink systems were measured. The thermochromic effect of the TLC ink and hybrid systems was analysed. Microscopy was used to display the visual colour play effect and the effect of the fluorescence. Results of the measurements showed high compatibility of used materials in the proposed hybrid ink systems. Since the effect of luminescence and the colour play effect in the hybrid systems were preserved, it can be concluded that TLC/UVF hybrid ink systems can find their application in the development of functional packaging and in all other applications with special requirements for temperature monitoring and hidden information for different products.