Pickering emulsions are emulsions stabilized by solid particles, which generally provide a more stable system than traditional surfactants. Among various solid stabilizers, bio-based particles from renewable resources, such as micro- and nanofibrillated cellulose, may open up new opportunities for the future of Pickering emulsions owing to their properties of nanosize, biodegradability, biocompatibility, and renewability. The aim of this research was to obtain oil-in water (O/W) Pickering emulsions using cellulose microfibers (CMF) produced from cotton cellulose linters by mechanical treatment through a high-pressure homogenizer. The O/W Pickering emulsions were prepared with different O/W ratios by mixing edible oil (sunflower oil) with water containing CMF at concentrations of up to 1.0 wt%. The apparent viscosity of the separated emulsion phase was measured. Results showed the feasibility of using low concentration of CMF for preparing and stabilizing Pickering emulsions, with the apparent viscosity of the emulsion phase increasing 60–90 times with respect to the sunflower oil, for a shear rate of 1 s⁻¹. In addition, theoretical nutrition facts of the emulsions were calculated and compared with other fats used in foods, showing that they can be a promising low-calorie product containing dietary fiber, replacing trans and saturated fats in foods.

The recycled paper and board industry needs to improve the quality of their products to meet customer demands. The refining process and strength additives are commonly used to increase mechanical properties. Interfiber bonding can also be improved using cellulose nanofibers (CNF). A circular economy approach in the industrial implementation of CNF can be addressed through the in situ production of CNF using side cellulose streams of the process as raw material, avoiding transportation costs and reducing industrial wastes. Furthermore, CNF fit for use can be produced for specific industrial applications.This study evaluates the feasibility of using two types of recycled fibers, simulating the broke streams of two paper machines producing newsprint and liner for cartonboard, to produce in situ CNF for direct application on the original pulps, old newsprint (ONP), and old corrugated container (OCC), and to reinforce the final products. The CNF were obtained by 2,2,6,6-tetramethyl-1-piperidinyloxy (TEMPO)-mediated oxidation and homogenization at 600 bar. Handsheets were prepared with disintegrated recycled pulp and different amounts of CNF using a conventional three-component retention system. Results show that 3 wt.% of CNF produced with 10 mmol of NaClO per gram of dry pulp improve tensile index of ONP ~30%. For OCC, the same treatment and CNF dose increase tensile index above 60%. In both cases, CNF cause a deterioration of drainage, but this effect is effectively counteracted by optimising the retention system.

Recycling cycles cause a decrease in mechanical paper properties due to cellulose fiber degradation. The use of cellulose micro/nanofibers (CMF/CNF) to reinforce paper strength has been well studied, although it has been found to have negative effects on drainage. However, the application of CMF/CNF as paper reinforcement is affected by the nanocellulose type. Thus in this study mechanical and chemical treatments in CNF production were compared. Old corrugated container (OCC) pulp used to produce recycled cartonboard was reinforced with 1) CMF from never-dried northern bleached softwood kraft pulp (NBSK) highly refined in a 16-inch low consistency refiner at 1200 rpm and 25 kW of net power; and 2) CNF from NBSK pulp treated by TEMPO-mediated oxidation and homogenization at 600 bars. CMF/CNF and OCC were pulped at the same time and handsheets formed with cationic starch (CS) as retention system. Mechanical, drainage and flocculation properties were evaluated and compared. Data were also compared with other sources of TEMPO CNF. Results show an improvement in mechanical properties, drainage and flocculation when OCC is reinforced with CMF obtained with LCR. Therefore, high fibrillation was not necessary to improve mechanical paper or cardboard properties.