The attractiveness of additive manufacturing (AM) relates to the ability of this technology to rapidly produce very complex components at affordable costs. However, the properties and corrosion behavior, in particular, of products produced by AM technology should at least match the properties obtained by conventional technologies. The present study aims at evaluating the corrosion behavior and corrosion fatigue endurance of AlSi10Mg alloy produced by selective laser melting (SLM) in comparison with its conventional counterpart, gravity cast alloy. The results obtained indicate that the corrosion resistance of the printed and cast alloys was relatively similar, with a minor advantage to the printed alloy. The corrosion fatigue endurance of the printed alloy was relatively improved compared to the cast alloy. This was mainly attributed to the significant differences between the microstructure and defect characteristics of those two alloys.

Current additive manufacturing (AM) processes are mainly focused on powder bed technologies, such as electron beam melting (EBM) and selective laser melting (SLM). However, the main disadvantages of such techniques are related to the high cost of metal powder, the degree of energy consumption, and the sizes of the components, that are limited by the size of the printing cell. The aim of the present study was to evaluate the environmental behavior of low carbon steel (ER70S-6) produced by a relatively inexpensive AM process using wire feed arc welding. The mechanical properties were examined by tension testing and hardness measurements, while microstructure was assessed by scanning electron microscopy and X-ray diffraction analysis. General corrosion performance was evaluated by salt spray testing, immersion testing, potentiodynamic polarization analysis, and electrochemical impedance spectroscopy. Stress corrosion performance was characterized in terms of slow strain rate testing (SSRT). All corrosion tests were carried out in 3.5% NaCl solution at room temperature. The results indicated that the general corrosion resistance of wire arc additive manufacturing (WAAM) samples were quite similar to those of the counterpart ST-37 steel and the stress corrosion resistance of both alloys was adequate. Altogether, it was clearly evident that the WAAM process did not encounter any deterioration in corrosion performance compared to its conventional wrought alloy counterpart.

This study aims at evaluating the effect of microstructure imperfections on the corrosion fatigue performance of an ER70S-6 alloy produced by wire arc additive manufacturing (WAAM) process, in a 3.5% NaCl solution. For reference, a regular ST-37 alloy with relatively similar chemical composition was considered as a counterpart alloy. This was justified by the fact that the ER70S-6 alloy is usually used for conventional welding of ST-37 steel. The results obtained indicated that while the ST-37 alloy exhibited fatigue strength of 240 MPa in the corrosive solution, the additively manufactured ER70S-6 alloy showed fatigue strength of only 140 MPa. These differences were related to microstructural imperfections that are inherently produced during the WAAM process.

The growing interest in refractory high-entropy alloys (HEAs) in the last decade is mainly due to their thermal stability, outstanding mechanical properties, and excellent corrosion resistance. However, currently HEAs are still not considered for use as common structural materials due to their inherent drawbacks in terms of processing and machining operations. The recent progress witnessed in additive manufacturing (AM) technologies has raised the option of producing complex components made of HEAs with minimal machining processes. So far, this could be achieved by using pre-alloyed powders of HEAs that were mainly produced by a conventional arc melting furnace (AMF) in the form of small compounds that were transformed into powder via a gas atomization process. To significantly reduce the production cost, the present study aims to analyze the ability to synthesize HEA WTaMoNbV via a laser powder bed fusion (LPBF) process using mixed elemental alloying powder as the raw material. For comparison, a counterpart alloy with the same chemical composition was analyzed and produced by an AMF process. The microstructures of the tested alloys were examined by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD) analyses. The physical properties were evaluated in terms of density and mechanical strength, while the electrochemical behavior was assessed by potentiodynamic polarization analysis. The results disclosed similarities in microstructure, physical properties and electrochemical behavior between HEA WTaMoNbV manufactured by the proposed LPBF process and its counterpart alloy produced by an AMF process.