Bacteria are one of the significant causes of infection in the body after scaffold implantation. Effective use of nanotechnology to overcome this problem is an exciting and practical solution. Nanoparticles can cause bacterial degradation by the electrostatic interaction with receptors and cell walls. Simultaneously, the incorporation of antibacterial materials such as zinc and graphene in nanoparticles can further enhance bacterial degradation. In the present study, zinc-doped hydroxyapatite/graphene was synthesized and characterized as a nanocomposite material possessing both antibacterial and bioactive properties for bone tissue engineering. After synthesizing the zinc-doped hydroxyapatite nanoparticles using a mechanochemical process, they were composited with reduced graphene oxide. The nanoparticles and nanocomposite samples were extensively investigated by transmission electron microscopy, X-ray diffraction, and Raman spectroscopy. Their antibacterial behaviors against Escherichia coli and Staphylococcus aureus were studied. The antibacterial properties of hydroxyapatite nanoparticles were found to be improved more than 2.7 and 3.4 times after zinc doping and further compositing with graphene, respectively. In vitro cell assessment was investigated by a cell viability test and alkaline phosphatase activity using mesenchymal stem cells, and the results showed that hydroxyapatite nanoparticles in the culture medium, in addition to non-toxicity, led to enhanced proliferation of bone marrow stem cells. Furthermore, zinc doping in combination with graphene significantly increased alkaline phosphatase activity and proliferation of mesenchymal stem cells. The antibacterial activity along with cell biocompatibility/bioactivity of zinc-doped hydroxyapatite/graphene nanocomposite are the highly desirable and suitable biological properties for bone tissue engineering successfully achieved in this work.

The material for bone scaffold replacement should be biocompatible and antibacterial to prevent scaffold-associated infection. We biofunctionalized the hydroxyapatite (HA) properties by doping it with lithium (Li). The HA and 4 Li-doped HA (0.5, 1.0, 2.0, 4.0 wt.%) samples were investigated to find the most suitable Li content for both aspects. The synthesized nanoparticles, by the mechanical alloying method, were cold-pressed uniaxially and then sintered for 2 h at 1250 °C. Characterization using field-emission scanning electron microscopy (FE-SEM) revealed particle sizes in the range of 60 to 120 nm. The XRD analysis proved the formation of HA and Li-doped HA nanoparticles with crystal sizes ranging from 59 to 89 nm. The bioactivity of samples was investigated in simulated body fluid (SBF), and the growth of apatite formed on surfaces was evaluated using SEM and EDS. Cellular behavior was estimated by MG63 osteoblast-like cells. The results of apatite growth and cell analysis showed that 1.0 wt.% Li doping was optimal to maximize the bioactivity of HA. Antibacterial characteristics against Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) were performed by colony-forming unit (CFU) tests. The results showed that Li in the structure of HA increases its antibacterial properties. HA biofunctionalized by Li doping can be considered a suitable option for the fabrication of bone scaffolds due to its antibacterial and unique bioactivity properties.

In this paper, an effective method was employed for preparation of nanofibers using conducting polymer-functionalized reduced graphene oxide (rGO). First, graphene oxide (GO) was obtained from graphite by Hommer method. GO was reduced to rGO by NaBH₄ and covalently functionalized with a 3-thiophene acetic acid (TAA) by an esterification reaction to reach 3-thiophene acetic acid-functionalized reduced graphene oxide macromonomer (rGO-f-TAAM). Afterward, rGO-f-TAAM was copolymerized with 3-dodecylthiophene (3DDT) and 3-thiophene ethanol (3TEt) to yield rGO-f-TAA-co-PDDT (rGO-g-PDDT) and rGO-f-TAA-co-P3TEt (rGO-g-PTEt), which were confirmed by Fourier transform infrared spectra. The grafted materials depicted better electrochemical properties and superior solubilities in organic solvents compared to GO and rGO. The soluble rGO-g-PDDT and rGO-g-PTEt composites blended with polycaprolactone were fabricated by electrospinning, and then cytotoxicity, hydrophilicity, biodegradability and mechanical properties were investigated. The grafted rGO composites exhibited a good electroactivity behavior, mainly because of the enhanced electrochemical performance. The electrospun nanofibers underwent degradation about 7 wt% after 40 days, and the fabricated scaffolds were not able to induce cytotoxicity in mouse osteoblast MC3T3-E1 cells. The soluble conducting composites developed in this study are utilizable in the fabrication of nanofibers with tissue engineering application.