Interfacial Characterization and Optimal Preparation of Novel Bamboo Plastic Composite Engineering Materials

A bio-inspired approach to coating polydopamine (PDA) onto bamboo fiber (BF) was developed to enhance the poor interfacial bonding of BF/polybutylene succinate (PBS) biocomposites. The macroscopic features, functional groups, nanoscale topography, and crystallinity of the PDA-coated BF (D-BF) were investigated with digital photography, Fourier transform infrared (FTIR) spectroscopy, atomic force microscopy (AFM), and X-ray diffraction (XRD), respectively. The effects of the PDA loading rate on the performance of the D-BF/PBS biocomposites were also evaluated through the mechanical properties tests, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA), and scanning electron microscopy (SEM). Treating BF with an optimum concentration of dopamine (DOPA) decreased the polarity of the bamboo fiber, while maintaining the crystal structure of the cellulose. The thermal stability, mechanical properties, and storage modulus of the D-BF/PBS biocomposites were noticeably enhanced because of the good interfacial compatibility. Moreover, the glass transition temperature (Tg) and crystallinity of the biocomposites increased with higher DOPA loading rates. The best properties were observed with a DOPA concentration of 1.0 mg/mL. These findings exhibited the feasibility for the application of PDA in the biomass fiber-reinforced biodegradable polymer composites industry.

New plywood composites for furniture and interior decoration were developed with eucalyptus veneers using polyethylene films as formaldehyde-free adhesives. To enhance the interfacial adhesion, the veneers were modified with an oven treatment (temperature: 100, 120, 140, and 160 °C; time: 0.5, 1.0, 1.5, and 2.0 h) or by soaking in a sodium hydroxide (NaOH) solution (concentration: 3%, 7%, and 11%; time: 12, 24, and 36 h). The effects of these treatments on the mechanical properties (flexural strength, MOR; flexural modulus, MOE; wet shear strength, WSS) of the composites were studied. Both treatments improved the three properties of the composites. The heat treatment was better at improving the shear property, while the alkali treatment was better at improving the flexural properties. For the heat treatment, the highest WSS was 81.1% higher than the untreated group. The optimum conditions for the heat treatment were 140 °C and 1.0 h. For the alkali treatment, the highest MOR and MOE were 267.5% and 173.7% higher than the untreated group, respectively. The optimum conditions for the alkali treatment were 3% and 36 h. The changes to the veneer surfaces were determined by scanning electron microscopy.