The battery energy storage system (BESS) market is growing rapidly around the world. Lithium Nickel Cobalt Manganese Oxide (LiNiCoMnO₂) is attracting attention due to its excellent energy density, high output power, and fast response characteristics. It is being extensively researched and is finding use in many applications, such as in electric vehicles (EV) and energy storage systems (ESS). The performance and lifetime characteristics of a battery change for varying Ni contents. The consideration of these characteristics of a battery allow for a more reliable battery management system (BMS) design. In this study, various experiments and analyses were carried out using a lithium-ion battery (NCM LIB) with differing Ni contents. In particular, the following two combinations were studied: LiNi_0.5Co_0.2Mn_0.3O₂(NCM523) and LiNi_0.6Co_0.2Mn_0.2O₂ (NCM622). Various analyses were performed, such as C-rate (C-rate is the charge-discharge rate of a battery relative to nominal capacity) performance tests, hybrid pulse power characterization (HPPC), accelerated deterioration experiments, electrochemical impedance spectroscopy (EIS), parameter estimations of battery equivalent circuits through alternating current (AC) and direct current (DC) impedance, and comparative analyses of battery modeling.

Rice husk is produced in a massive amount worldwide as a byproduct of rice cultivation. Rice husk contains approximately 20 wt% of mesoporous SiO2. We produce mesoporous silicon (Si) by reducing the rice husk-originating SiO2 using a magnesio-milling process. Taking advantage of meso-porosity and large available quantity, we apply rice husk-originating Si to lithium ion battery anodes in a composite form with commercial graphite. By varying the mass ratio between these two components, trade-off relation between specific capacity and cycle life was observed. A controllable pre-lithiation scheme was adopted to increase the initial Coulombic efficiency and energy density. The series of electrochemical results suggest that rice husk-originating Si–graphite composites are promising candidates for high capacity lithium ion battery anodes, with the prominent advantages in battery performance and scalability.