The aim of the article is to analyze the influence of short coir, glass and carbon fiber admixture on the mechanical properties of fly ash-based geopolymer, such as: flexural and compressive strength. Glass fiber and carbon fibers have been chosen due to their high mechanical properties. Natural fibers have been chosen because of their mechanical properties as well as for the sake of comparison between their properties and the properties of the artificial ones. Fourth series of fly ash-based geopolymers for each fiber was cast: 1, 2, and 5% by weight of fly ash and one control series without any fibers. Each series of samples were tested on flexural and compressive strength after 7, 14, and 28 days. Additionally, microstructural analysis was carried out after 28 days. The results have shown an increase in compressive strength for composites with fibers—an improvement in properties between 25.0% and 56.5% depending on the type and amount of fiber added. For bending strength, a clear increase in the strength value is visible for composites with 1 and 2% carbon fibers (62.4% and 115.6%). A slight increase in flexural strength also occurred for 1% addition of glass fiber (4.5%) and 2% addition of coconut fibers (5.4%). For the 2% addition of glass fibers, the flexural strength value did not change compared to the value obtained for the matrix material. For the remaining fiber additions, i.e., 5% glass fiber as well as 1 and 5% coconut fibers, the flexural strength values deteriorated. The results of the research are discussed in a comparative context and the properties of the obtained composites are juxtaposed with the properties of the standard materials used in the construction industry.

In recent years, 3D concrete printing technology has been developing dynamically. Intensive research is still being carried out on the composition of the materials dedicated to innovative 3D printing solutions. Here, for the first time, concrete-geopolymer hybrids produced with 3D printing technology and dedicated environmentally friendly building construction are presented. The concrete-geopolymer hybrids consisting of 95% concrete and 5% geopolymer based on fly ash or metakaolin were compared to standard concrete. Moreover, 3D printed samples were compared with the samples of the same composition but prepared by the conventional method of casting into molds. The phase composition, water leachability, compressive, and flexural strength in the parallel and perpendicular directions to the printing direction, and fire resistance followed by compressive strength were evaluated. Concrete-geopolymer hybrids were shown to contain a lower content of hazardous compounds in leaches than concrete samples. The concentration of toxic metals did not exceed the limit values indicated in the Council Decision 2003/33/EC; therefore, the materials were classified as environmentally neutral. The different forms of Si/Al in fly ash and metakaolin resulted in the various potentials for geopolymerization processes, and finally influenced the densification of the hybrids and the potential for immobilization of toxic elements. Although the compressive strength of concrete was approximately 40% higher for cast samples than for 3D printed ones, for the hybrids, the trend was the opposite. The addition of fly ash to concrete resulted in a 20% higher compressive strength compared to an analogous hybrid containing the addition of metakaolin. The compressive strength was 7–10% higher provided the samples were tested in the parallel direction to the Z-axis of the printout. The sample compressive strength of 24–43 MPa decreased to 8–19 MPa after the fire resistance tests as a result of moisture evaporation, weight loss, thermal deformation, and crack development. Importantly, the residual compressive strength of the hybrid samples was 1.5- to 2- fold higher than the concrete samples. Therefore, it can be concluded that the addition of geopolymer to the concrete improved the fire resistance of the samples.

In the era of increasing climatic requirements and changing approaches towards circular economy (CE), the demand for materials designed with care for the environment is growing. This idea is especially important in the construction industry, where ordinary Portland cement (OPC) production emits a large number of greenhouse gases. The main aim of this article is to demonstrate the possibility of using industrial waste for geopolymer production according to CE goals, including closing material loops. This work is based on a critical analysis of the literature and selected case studies. The most important findings of this article allow us to confirm that the role of industrial waste in the construction industry is growing and that industrial by-products are valuable sources for geopolymer production. The development of sustainable materials allows the introduction of closed loops into production processes by making it possible to reuse materials after the end of use, which is an important issue in the context of introducing CE into practice, especially in existing systems.

Geopolymer concretes can be a viable alternative to conventional Portland cement-based materials. In their design, it is important to maintain an appropriate liquid-to-solid ratio (L/S), which affects several properties, such as the compressive strength, water absorption, and frost resistance. The objective of this paper is to analyze the influence of the fly-ash and metakaolin precursor types for three different L/S ratios: 0.30, 0.35, and 0.45. The results of the physical and mechanical properties, including the apparent density and compressive strength, as well the durability parameters, including frost resistance and water penetration depth, are presented in this paper. It was found that as the L/S ratio decreased, the average compressive strength increased for all materials. After freeze–thaw cycles, decreases in the compressive strength properties were observed for all types of materials—metakaolin- and fly ash-based—irrespective of the L/S ratio. Moreover, the frost resistance of geopolymers increased with the increase in the L/S ratio. The printability of the mixes was also verified in order to confirm the application of the developed materials to additive manufacturing processes.

Zeolites obtained from fly ash are characterized by very good anion- and cation-exchange properties and a developed porous structure. This paper presents the results of surface modification studies of synthetic zeolites obtained from calcined coal shale (clay materials). Calcium compounds and hexadecyltrimethylammonium bromide (HDTMA) were used as modifying substances. The characteristics of the raw material and the zeolite obtained as a result of its synthesis are presented. The surface modification method is described. Furthermore, the results of sorption and desorption of NO₃, PO₄, and SO₄ from raw and modified samples are presented. The results of anion- and cation-exchange capacities for other zeolite types were also compared. Modification of the materials with Ca ions and HDTMA surfactant only improved the sorption of sulfates. The 90% desorption of nitrates, phosphates, and sulphates from the zeolite material without modification indicates a good release capacity of these compounds and their potential use as fertilizer additives.

The purpose of this study is to synthesize geopolymer binders as an environmentally friendly alternative to conventional cement using available local raw materials. Waste materials such as chalcedonite (Ch), amphibolite (A), fly ash from lignite combustion (PB), and diatomite dust (D) calcined at 900 °C were used to produce geopolymer binders. Metakaolin (M) was used as an additional modifier for binders based on waste materials. The base materials were subjected to fluorescence X-ray fluorescence (XRF) analysis and X-ray diffractometry (XRD) to determine chemical and phase composition. A laser particle size analysis was also performed. The various mixtures of raw materials were activated with a 10 M solution of NaOH and sodium water glass and then annealed for 24 h at 60 °C. The produced geopolymer binders were conditioned for 28 days under laboratory conditions and then subjected to microstructural analysis (SEM) and flexural and compressive strength tests. The best compressive strength results were obtained by the Ch + PB samples—more than 57 MPa, while the lowest results were obtained by the Ch + D+A + M samples—more than 20 MPa. On the other hand, as a result of the flexural strength tests, the highest flexural results were obtained by D + A + M + PB binders—more than 12 MPa, and the lowest values were obtained by binders based on Ch + D+A + M—about 4.8 MPa.