Conventional material processing approaches often achieve strengthening of materials at the cost of reduced ductility. Here, we show that high-pressure and high-temperature (HPHT) treatment can help overcome the strength-ductility trade-off in structural materials. We report an initially strong-yet-brittle eutectic high entropy alloy simultaneously doubling its strength to 1150 MPa and its tensile ductility to 36% after the HPHT treatment. Such strength-ductility synergy is attributed to the HPHT-induced formation of a hierarchically patterned microstructure with coherent interfaces, which promotes multiple deformation mechanisms, including dislocations, stacking faults, microbands and deformation twins, at multiple length scales. More importantly, the HPHT-induced microstructure helps relieve stress concentration at the interfaces, thereby arresting interfacial cracking commonly observed in traditional eutectic high entropy alloys. These findings suggest a new direction of research in employing HPHT techniques to help develop next generation structural materials.

Grain boundaries (GBs) serve not only as strong barriers to dislocation motion, but also as important carriers to accommodate plastic deformation in crystalline solids. During deformation, the inherent excess volume associated with loose atomic packing in GBs brings about a microscopic degree of freedom that can initiate GB plasticity, which is beyond the classic geometric description of GBs. However, identification of this atomistic process has long remained elusive due to its transient nature. Here, we use Au polycrystals to unveil a general and inherent route to initiating GB plasticity via a transient topological transition process triggered by the excess volume. This route underscores the general impact of a microscopic degree of freedom which is governed by a stress-triaxiality-based criterion. Our findings provide a missing perspective for developing a more comprehensive understanding of the role of GBs in plastic deformation.