Even in the 21st century, dental caries is considered a global burden, severely upsetting the health and quality of life of those affected. Apart from the usage of fluoride and regular oral hygiene, one of the most important prophylactic approaches against the occurrence of caries is the sealing of pits and fissures. However, the rapid progress of new materials and applications for sealing pits and fissures also raises new questions about their correct application. Recent literature on pit and fissure sealing, caries prevention, as well as caries risk assessment for both children and adults was reviewed. This report provides a general overview of pit and fissure sealing, the materials used for sealing occlusal surfaces, as well as indications and possible side effects. The conclusions are that sealing pit and fissures of primary and permanent teeth is an effective method for preventing and arresting caries. However, regular checkups must be conducted to avoid advanced tooth decay attributable to leakages in the sealing.

SUMMARY: Objective: This study evaluated the differences in enamel color change, surface hardness, elastic modulus, and surface roughness between treatments with four bleaching gels containing carbamide peroxide (two at 10% and one each at 35%, and 45%) and two bleaching gels containing hydrogen peroxide (two at 40%). Methods: Enamel specimens were bleached and color changes were measured. Color change was calculated using either ΔE or the Bleaching Index (BI). Then, surface hardness, elastic modulus, and surface roughness of the enamel specimens were evaluated. All measurements were performed at baseline and directly after the first bleaching treatment for all carbamide peroxide– and hydrogen peroxide–containing bleaching gels. In addition, final measurements were made 24 hours after each of a total of 10 bleaching treatments for carbamide peroxide bleaching gels, and 1 week after each of a total of three bleaching treatments for hydrogen peroxide bleaching gels. Results: After the last bleaching treatment, respective ΔE scores were 17.6 and 8.2 for the two 10% carbamide peroxide gels, 12.9 and 5.6 for the 45% and 35% carbamide peroxide gels, and 9.6 and 13.9 for the two 40% hydrogen peroxide gels. The respective BI scores were −2.0 and −2.0 for the two 10% carbamide peroxide gels, −3.5 and −1.5 for the 45% and 35% carbamide peroxide gels, and −2.0 and −3.0 for the two 40% hydrogen peroxide gels. Each bleaching gel treatment resulted in significant whitening; however, no significant difference was found among the gels after the last bleaching. Whitening occurred within the first bleaching treatments and did not increase significantly during the remaining treatments. Surface hardness significantly decreased after the last bleaching treatment, when 10% carbamide peroxide was used. Furthermore, significant changes in the elastic modulus or surface roughness occurred only after treatment with 10% carbamide peroxide. Conclusion: All six bleaching gels effectively bleached the enamel specimens independent of their concentration of peroxide. Gels with low peroxide concentration and longer contact time negatively affected the enamel surface.

Purpose of this study was to evaluate the accuracy of fit of cemented polymer infiltrated ceramic network (PICN) material crowns manufactured after digital and conventional impression techniques using micro computed tomography (CT). Furthermore to determine the cement space volume and porosities in the cement layer. A molar typodont tooth was prepared for PICN material crowns and replicated thirty times. The dies were randomly divided into three groups of 10 specimens each according to the impression technique: 3M True Definition Scanner (TDS), cara TRIOS (Trios) and Impregum Penta Soft (Impregum). PICN material crowns were milled for each specimen from Vita Enamic blocks and cemented on their respective dies. The absolute marginal discrepancy (AMD), internal fit (IG), total cement space volume (TVC) and marginal porosities (VP) were measured using Micro-CT. Mean and standard deviations values in μm for the AMD were: TDS 140.1 (28.4); Trios 253.7 (56.8); Impregum 220.2 (101.1). IG values in μm: TDS 173.1 (27.7); Trios 222.2 (22.4); Impregum 211.6 (55.9). TVC in mm3: TDS 19.82 (2.9); Trios 23.67 (2.01); Impregum 23.77 (5.09). VP in mm3: TDS 0.38 (0.09); Trios 0.36 (0.10); Impregum 0.51 (0.31). TDS group showed significantly better marginal and internal fit than the Trios group. No difference of the parameters was detected between the Impregum and both digital groups which implies that the digital impression technique is suitable in the manufacturing process of PICN material crowns.

Objectives: The study evaluates the influence of two spacer settings and three resin luting materials on the marginal and internal fit of polymer-infiltrated ceramic network (PICN) material crowns manufactured using a complete digital workflow. Methods: Optical impressions of fifty identical dies were performed using the 3M scanner (software version 5.0.2). Twenty crowns were designed using Ceramill Mind (version 3.4.10.1163), from which ten with spacer setting of 50 μm (G1) and ten with 80 μm (G2). Thirty crowns (spacer setting of 50 μm) were divided into three groups corresponding to the resin materials used as follows: RelyX Unicem (RX), Variolink Esthetic (VLE), and Nexus 3 (NX3). All crowns were milled from Vita Enamic blocks. After micro-CT scanning, absolute marginal discrepancy (AMD), internal gap (IG), total cement space volume (TCV), and marginal porosities (VP) were measured. Results: Significant difference was detected on the VP between the RX and NX3 group (p = 0.033). The mean values of all parameters were the following: AMD (μm): G1 182.6, G2 253.7, RX 210.8, VLE 195.5, NX3 186.6; IG (μm): G1 215.6, G2 173.1, RX 171.1, VLE 198.6, NX3 203; TCV (mm³): G1 22.9, G2 20.49, RX 17.57, VLE 17.49, NX3 20.59; VP (mm³): G1 0.26, G2 0.34, RX 0.32, VLE 0.46, NX3 0.54. Conclusions: Fit of PICN material crowns was not significantly influenced by increasing the spacer settings and cementation with different resin materials. Additionally, RelyX Unicem showed significantly less porosities as compared with Nexus3. Clinical relevance: Both 50 μm and 80 μm virtual spacer settings can be suggested for the manufacture of PICN crowns when Ceramill Mind (version 3.4.10.1163) is used. Furthermore, a self-adhesive system can be recommended for the cementation.