The detrimental effects of hardening in asphalt pavements were first recognized by pioneering pavement engineers in the 1900s and have been studied extensively during the last 70 years. This hardening process, referred to as asphalt aging, is generally defined as change in the rheological properties of asphalt binders/mixtures due to changes in chemical composition during construction and its service life period. Aging causes the asphalt material to stiffen and embrittle, which affects the durability and leads to a high potential for cracking. This paper presents the state of the art on asphalt and asphalt mixture aging and use of antioxidant additives to retard the aging. A picture of complex molecular structure of asphalt and its changes due to atmospheric condition and various protocols used to simulate aging in laboratory environment are also discussed. Emphasis is given on recent studies on simulation of aging of asphalt mixtures as there has been limited research on mixtures compared to the asphalt binder. Finally, this paper presents the application of antiaging techniques and its mechanism, use of various types of antioxidant additives to retard aging of asphalt and, hence, improve the performance of asphalt pavements.

Typically, aggregate gradation is selected to meet Superpave mix design specification; however, many Superpave mixtures have exhibited deficient field performance. The porosity of the dominant aggregate size range (DASR), which is the primary structural network of aggregates, has been extensively validated as a tool to evaluate coarse aggregate structure of laboratory and field asphalt mixtures. Mixtures identified by the system as having poor or marginal gradations resulted in poor rutting resistance. This study focused on how asphalt mixture performance is affected by changes in interstitial component (IC), which is the material between DASR particles. Laboratory testing clearly showed that IC characteristics may have a significant effect on rutting and cracking performance of mixtures. The disruption factor (DF) was developed to evaluate the potential of IC aggregates to disrupt the DASR structure. DF satisfactorily distinguished poor performing mixtures; therefore, it may eventually be used in combination with DASR porosity as a design parameter for rutting and cracking resistant asphalt mixtures.

Noise pollution due to highway traffic has drawn the attention of transportation agencies worldwide. Noise pollution is an irritant to residents, especially in urban areas near roads with high traffic volume. In addition to its adverse effects on the quality of life, traffic noise can induce stress that could lead to sleep disturbance and anxiety. Traditionally, noise barrier walls have been used for highways to mitigate traffic noise. However, using barrier walls as a noise abatement measure has proven to be very expensive. In addition to the cost, noise barrier walls are not always effective because they must break the line of sight to work properly, which is not always possible in case of intersections or driveways. Therefore, researchers especially from Europe and USA have been very proactive to reduce the noise at source. A number of research studies show traffic noise can be reduced by using an alternative surface type or changing texture of the pavement while complying with other requirements of sustainability, i.e., safety, structural durability, construction and maintenance costs. This paper presents a comprehensive review of the research conducted on this subject. A review of the tire-pavement noise generation and amplification mechanism, various traffic noise measurement methods and correlation among these methods, in addition to the abatement techniques used by various agencies to reduce pavement noise, is also presented.

The rheological properties of asphalt binders change with aging. Aging is accelerated at elevated temperatures due to binder oxidation, leading to fatigue cracking and eventually pavement failure under heavy and repeated traffic loading. This study examined the effect of various antioxidant additives and copolymers with antioxidant agents on retarding the aging of asphalt binders. The performance of antioxidants was evaluated at the binder and mastic levels. Two unmodified binders were tested and fine asphalt mixtures made with these binders and three different aggregates were prepared and evaluated. Fatigue characteristics of asphalt binders and fine portion of asphalt mixtures (FAM) were determined before and after aging and an aging index was defined to evaluate the effect of antioxidants and copolymers on aging. The results showed that certain antioxidants and copolymers such as Redicote AP, Solprene and Calprene may retard the aging and improve the rheological properties of the asphalt binders. In addition, the results of FAM testing confirmed the favourable effect of certain antioxidants on improving the resistance to fatigue. In addition, the type of aggregate was found to influence the rate of aging of asphalt mixtures.