The ability of TiO₂ to generate reactive oxygen species under UV radiation makes it an efficient candidate in antimicrobial studies. In this context, the preparation of TiO₂ microparticles coated with Ca- and Cu-based composite layers over which Cu(II), Cu(I), and Cu(0) species were identified is presented here. The obtained materials were characterized by a wide range of analytical methods, such as X-ray diffraction, electron microscopy (TEM, SEM), X-ray photoelectron (XPS), and UV-VIS spectroscopy. The antimicrobial efficiency was evaluated using qualitative and quantitative standard methods and standard clinical microbial strains. A significant aspect of this composite is that the antimicrobial properties were evidenced both in the presence and absence of the light, as result of competition between photo and electrical effects. However, the antibacterial effect was similar in darkness and light for all samples. Because no photocatalytic properties were found in the absence of copper, the results sustain the antibacterial effect of the electric field (generated by the electrostatic potential of the composite layer) both under the dark and in light conditions. In this way, the composite layers supported on the TiO₂ microparticles’ surface can offer continuous antibacterial protection and do not require the presence of a permanent light source for activation. However, the antimicrobial effect in the dark is more significant and is considered to be the result of the electric field effect generated on the composite layer.

The primary objective of this research was to develop efficient solid catalysts that can directly convert the lactic acid (LA) obtained from lignocellulosic biomass into alanine (AL) through a reductive amination process. To achieve this, various catalysts based on ruthenium were synthesized using different carriers such as multi-walled carbon nanotubes (MWCNTs), beta-zeolite, and magnetic nanoparticles (MNPs). Among these catalysts, Ru/MNP demonstrated a remarkable yield of 74.0% for alanine at a temperature of 200 °C. This yield was found to be superior not only to the Ru/CNT (55.7%) and Ru/BEA (6.6%) catalysts but also to most of the previously reported catalysts. The characterization of the catalysts and their catalytic results revealed that metallic ruthenium nanoparticles, which were highly dispersed on the external surface of the magnetic carrier, significantly enhanced the catalyst’s ability for dehydrogenation. Additionally, the -NH₂ basic sites on the catalyst further facilitated the formation of alanine by promoting the adsorption of acidic reactants. Furthermore, the catalyst could be easily separated using an external magnetic field and exhibited the potential for multiple reuses without any significant loss in its catalytic performance. These practical advantages further enhance its appeal for applications in the reductive amination of lactic acid to alanine.

Preventing and controlling the spread of multidrug-resistant (MDR) bacteria implicated in healthcare-associated infections is the greatest challenge of the health systems. In recent decades, research has shown the need for passive antibacterial protection of surfaces in order to reduce the microbial load and microbial biofilm development, frequently associated with transmission of infections. The aim of the present study is to analyze the efficiency of photocatalytic antimicrobial protection methods of surfaces using the new photocatalytic paint activated by light in the visible spectrum. The new composition is characterized by a wide range of analytical methods, such as UV-VIS spectroscopy, electron microscopy (SEM), X-ray powder diffraction (PXRD) or X-ray photoelectron spectroscopy (XPS). The photocatalytic activity in the UV-A was compared with the one in the visible light spectrum using an internal method developed on the basis of DIN 52980: 2008-10 standard and ISO 10678—2010 standard. Migration of metal ions in the composition was tested based on SR EN1186-3: 2003 standard. The new photocatalytic antimicrobial method uses a type of photocatalytic paint that is active in the visible spectral range and generates reactive oxygen species with inhibitory effect against all tested microbial strains.

Ruthenium-based catalysts were prepared through a deposition–precipitation approach, taking beta zeolites with Si/Al ratios of 12.5, 18.5, and 150, respectively, as supports, and 1–3 wt% loadings of metal. Their activation was performed in the presence of either H₂ or NaBH₄. The dispersion of the Ru species and the acid–base properties were influenced by both the preparation method and the activation protocol. The catalysts reduced under H₂ flow presented well-dispersed Ru(0) and RuO_x nanoparticles, while the reduction with NaBH₄ led to larger RuO_x crystallites and highly dispersed Ru(0). These characteristics exerted an important role in the hydrogenation of levulinic acid (LA) to γ-valerolactone (GVL). The H₂ dissociation occurred via a heterolytic mechanism involving Lewis acid–base pairs associated with RuO_x and the framework oxygen (Si-O-Al) located near the zeolite pore edge. The Ru(0) nanoparticles activated the –C=O bond of the LA substrate, while the presence of the carrier zeolite Brønsted acid sites promoted the ring-closure esterification of the 4-hydroxyvaleric acid (4-HVA) intermediate to GVL. An optimal combination of these features was achieved for the catalyst with 3 wt% Ru and a Si/Al ratio of 150, which selectively converted LA (X_LA = 96.5%) to GVL (S_GVL = 97.8%) at 130 °C and 10 bars of H₂.

The catalytic hydrotreatment of humins, the solid byproduct produced from the conversion of C6 sugars (glucose, fructose) to 5-hydroxymethylfurfural (HMF), using supported Pd@zeolite (Beta, Y, and USY) catalysts with different amounts of Pd (i.e., 0.5, 1.0 and 1.5 wt%) was investigated under molecular hydrogen pressure. The highest conversion of humins (52.0%) was obtained on 1.5Pd@USY catalyst while the highest amount of humins oil (27.3%) was obtained in the presence of the 1Pd@Beta zeolite sample, at P_H2 = 30 bars and T = 250 °C. The major compounds in the humins oil evidenced by GC-MS are alcohols, organic acids, ethers, and alkyl-phenolics. However, although all these classes of compounds are obtained regardless of the nature of the catalyst used, the composition of the mixture differs from one catalyst to another. Furanic compounds were not identified in the reaction products. A possible explanation may be related to their high reactivity under the reaction conditions, in the presence of the Pd-based catalysts these compounds lead to alkyl phenolics, important intermediates in the petrochemical industry.

Spin asymmetry is detected in clean Pt(001)–hex by spin-resolved photoelectron spectroscopy even in absence of external sample magnetization. Magnetization of the sample immediately after preparation yields a consistent remnant spin asymmetry in the direction of the applied magnetic field. The surfaces were also characterized by low energy electron diffraction, scanning tunneling microscopy and high resolution core level x-ray photoelectron spectroscopy, allowing one to quantify the surface component, attributed to the last surface layer enriched in electrons. The explanation of the spin asymmetry induced by electron accumulation into the last monolayer is sketched by using band ferromagnetism criteria. The orientation of the spin asymmetry in the nonmagnetized sample coincides with the direction of the rows of the hex reconstruction, while in the magnetized sample it is aligned with the direction of the external magnetizing field. A strong variation of the spin asymmetry as function of the binding energy near the Fermi level, whose amplitude depends also on the median emission angle, suggests a spin textured state in this energy range or the presence of a Stoner gap.