Monosulfoaluminate (Ca₄Al₂(SO₄)(OH)₁₂∙6H₂O) plays an important role in anion binding in Portland cement by exchanging its original interlayer ions (SO₄²⁻ and OH⁻) with chloride ions. In this study, scanning transmission X-ray microscope (STXM), X-ray absorption near edge structure (XANES) spectroscopy, and X-ray diffraction (XRD) were used to investigate the phase change of monosulfoaluminate due to its interaction with chloride ions. Pure monosulfoaluminate was synthesized and its powder samples were suspended in 0, 0.1, 1, 3, and 5 M NaCl solutions for seven days. At low chloride concentrations, a partial dissolution of monosulfoaluminate formed ettringite, while, with increasing chloride content, the dissolution process was suppressed. As the NaCl concentration increased, the dominant mechanism of the phase change became ion exchange, resulting in direct phase transformation from monosulfoaluminate to Kuzel’s salt or Friedel’s salt. The phase assemblages of the NaCl-reacted samples were explored using thermodynamic calculations and least-square linear combination (LC) fitting of measured XANES spectra. A comprehensive description of the phase change and its dominant mechanism are discussed.

Using ground granulated blast-furnace slag (GGBS) under different alkaline conditions, we studied the mechanisms and extents of Cr(VI) reduction and sorption and compared them to reactions with Portland cement (PC). We also investigated the effects of mixing PC/GGBS ratios on Cr(VI) dissolution after carbonating the substrates. We observed a complete sorption and reduction of Cr(VI) to Cr(III) in a GGBS-in-Ca(OH)₂ solution (pH > ~12.5) after 10 h, whereas in distilled water (pH = ~11.5) GGBS exhibited only marginal sorption and reduction (20%). Cr reactions with dissolved ions in supernatants derived from GGBS indicated that the anions dissolved from GGBS act as a reducing agent for Cr(VI) in a Ca(OH)₂ solution. Soft X-ray absorption microscopy identified a partial reduction of Cr(VI) to Cr(III) on the GGBS surface. The carbonation of pure PC paste substantially increased the amount of dissolved Cr(VI) in a solution phase whereas a 5 wt % replacement of PC with GGBS significantly reduced the amount of dissolved Cr(VI). We concluded that in the mixed paste during the early curing stage GGBS reduced a significant fraction of Cr(VI) to Cr(III) and that the Cr(III) adsorbed in the GGBS-PC mixture’s hydration products does not readily dissolve, even under carbonation conditions.