This work combines guanidine dihydrogen phosphate (GDP) and zinc borate (ZB) to modify wood via microwave-ultrasonic impregnation for realizing favorable flame retardancy and thermal stability, which were investigated by the limiting oxygen index (LOI), thermogravimetric analysis (TGA), and cone calorimetry tests (CONE). The treated samples show better performance in fire retardancy with the LOI value increasing to 47.8%, and the results of TGA indicate the outstanding thermal stability of wood. In addition, the decline of heat release rate, total heat release, smoke production rate, and total smoke production examined by CONE further demonstrates the achievement of excellent flame retardancy and smoke suppression properties of the GDP/ZB-modified wood.

Recently, widespread concern has been aroused on environmentally friendly materials. In this article, barium phytate (Pa-Ba) was prepared by the reaction of phytic acid with barium carbonate in deionized water, which was used to blend with intumescent flame retardant (IFR) as a flame retardant and was added to epoxy resin (EP). Afterward, the chemical structure and thermal stability of Pa-Ba were characterized by Fourier transform infrared (FTIR) spectroscopy and thermogravimetric analysis (TGA), respectively. On this basis, the flammability and flame retardancy of EP composites were researched. It is shown that EP/14IFR/2Ba composite has the highest limiting oxygen index (LOI) value of 30.7%. Moreover, the peak heat release rate (PHRR) of EP/14IFR/2Ba decreases by 69.13% compared with pure EP. SEM and Raman spectra reveal the carbonization quality of EP/14IFR/2Ba is better than that of other composites. The results prove that Pa-Ba can cooperate with IFR to improve the flame retardancy of EP, reducing the addition amount of IFR in EP, thus expanding the application range of EP. In conclusion, adding Pa-Ba to IFR is a more environmentally friendly and efficient method compared with others.

Density prediction is of great significance for molecular design of energetic materials, since detonation velocity linearly with density and detonation pressure increases with the density squared. However, the accuracy and generalization of former reported prediction models need further improvement, because most of them are derived from small data sets and few molecular descriptors. As shown in this paper, for molecules presenting brick-like shape or containing more hydrogen-bond donors the predicted densities have large negative deviations from experimental values. Thus, a molecular morphology descriptor η and a hydrogen-bond descriptor H_b are introduced as correction items to build 3 new QSPR models. Besides, 3694 nitro compounds are adopted as data set by this work. The accuracies are obviously improved, and the generalizations are verified by an independent test set. At the level of B3PW91/6-31G(d,p), the effective ratios (ERs) of the 3 Equations, for Δρ < 5%, are 92.7%, 91.8%, and 93.3%; for Δρ < 2%, the values are 53.5%, 51.3%, and 54.7%. At the level of B3LYP/6-31G**, for Δρ < 5%, the values are 92.3%, 91.4% and 92.9%; for Δρ < 2%, the values are 53.7%, 51.4% and 53.2%.

Acidizing retarders are used to reduce the reaction rate between hydrochloric acid (HCl) and carbonates to increase the efficiency of acidification of oil and gas wells and increase oil and gas recovery. We synthesized two polymeric acidizing retarders (AR-1 and AR-2) to explore ways to improve the efficiency of this process. Retarder AR-1 is based on acrylamide (AM) and allyl polyethylene glycol (APEG-1000), and retarder AR-2 is composed of AM, APEG-1000, and octadecyl dimethyl allyl ammonium chloride (C-18). The molecular structures of AR-1 and AR-2 were characterized by Fourier transform infrared (FT-IR) and ¹H nuclear magnetic resonance (¹H-NMR). The retarding performance and acid–rock reaction rates of AR-1 and AR-2 were evaluated, and the experimental results indicated that AR-2 had a better retarding performance than AR-1, and the acid–rock reaction rate of AR-1 was higher than AR-2. This could be because AR-2 with its hydrophobic chains forms a thicker adsorbed film. This was confirmed by X-ray photoelectron spectroscopy (XPS) and adsorption behavior studies. The scanning electron microscope (SEM) images, contact angle, and XPS results showed that both retarders form adsorption films on the surface of rocks, indicating that the introduction of AM and APEG-1000 makes the retarder adsorb on rock surfaces. The introduction of hydrophobic chains for AR-2 enhanced the thickness of adsorbed film, indicating that adding hydrophobic chains to the acidizing retarder significantly improves its retarding performance.

High-energy materials containing azole and furazan have revealed numerous properties; however, the underlying optical properties need to be solved. Meanwhile, the uncertainty for the choice of fluorescent matrix materials and the flexible situational conditions prompted us to estimate the optical and fluorescent properties of 5,5'-dinitro-2H,2H'-3,3'-bi-1,2,4-triazole (DNBT), 4,4'-dinitroazolefurazan (DNAF), and 4,4'-dinitro-3,3'-4,3'-ter-1,2,5-oxadiazole (DNTO). The first-principles calculation with improved dispersion correction terms and time-dependent density functional theory were utilized to calculate the absorbance and excitation energy of DNBT, DNAF, and DNTO, as well as characterization for their crystal structure, electronic structure, molecular orbitals, and so forth, synchronously. In this work, the absorbance anisotropy of DNBT and DNTO is stronger than that of DNAF. The absorbance for each of the (0,0,1) crystal planes in the three compounds is greater than that of the other two crystal planes. Moreover, DNBT has the maximum absorbance on the (0,0,1) crystal plane. The N-N-H from DNBT and N-O-N from DNTO and DNAF are responsible for these results, while N=N in DNAF weakens the performance of N-O-N. UV-vis spectra show that the maximum absorption wavelengths λ_max for DNBT, DNAF, and DNTO are 225, 228, and 201 nm, respectively. The number of five-membered rings and the coplanarity of groups in the intermolecular non-conjugation interaction potentially improve this ability due to the results from the crystal diffraction analysis. In addition, the polarization rate DNBT > DNTO > DNAF based on the molecular orbital analysis and the electrostatic potential calculation implies that the excitation energy of DNBT is less than DNTO, and the excitation energy of DNTO is less than DNAF. This work is beneficial to the expansion of energetic materials into the optical field and the accelerated application process of the related industry.

High-performance energetic materials are mainly used in the military, aerospace industry and chemical fields. The ordinary technology of producing energetic materials cannot avoid the domination of its unique needs. At present, revealing the underlying mechanism of the formation of high-energy materials is of great significance for improving their quality characteristics. We pay special attention to the decomposition and reactive molecular dynamics (RMD) simulation of 5,5′-dinitro-2H,2H′-3,3′-bi-1,2,4-triazole (DNBT). Various forms were captured in the simulation, and the form is determined by the temperature of the initial reactant. By observing the heating pattern and morphological changes under the initial thermal equilibrium, interesting temperature jumps were found in 325 K and 350 K. Observation of continuous heating (simulated temperatures are 2600 K, 2900 K, 3200 K and 3500 K) shows that DNBT has the maximum heating rate at 3500 K. In addition, N₂ occupies this dominant position in the product, moreover, N₂ and NO₂ respectively dominate the gas phase products during the initial heating process. According to the transition state analysis results of the intermediates, we found 4 interesting intermediate products, which were determined by high frequency reaction under the 4 simulated temperatures and performed with transition state calculations. It shows that the selection of reactant temperature and its activity is the key to orderly decomposition of DNBT. It is expected that these findings will be widely used in comprehensive decomposition devices and to improve the concept of learning military and industrial technology.