Flexible electronics is expected to be one of the most active research areas in the next decade. In this study, a mechanically strong and flexible epoxy/GnP composite film was fabricated having a percolation threshold of electrical conductivity at 1.08 vol% GnPs and high thermal conductivity as 1.07 W m ⁻¹ K ⁻¹ at 10 vol% GnPs. The composite film shows high mechanical performance: Young’s modulus and tensile strength were improved by 1344% and 66.7%, respectively, at 10 vol%. The film demonstrated high sensitivity to various mechanical loads: (i) it has gauge factors of 2 at strain range 0%–7% and 6 at range 7%–10%; (ii) it gives good electrical response with bending and twisting angles up to 180°; and (iii) it displays a good compressive load response up to 2 N where the absolute value of electrical resistance change increased by 71%. Furthermore, the film showed an excellent reliability up to 5.5 × 10 ³ cycles with minor zero-point error. Above 20 °C, the film solely acts as a temperature sensor; upon cyclic temperature testing, the film demonstrated a stable resistive response in the range of 30–75 °C with a temperature sensitivity coefficient of 0.0063 °C ⁻¹ . This flexible composite film has remarkable properties that enable it to be used as a full-fledged sensor for universal applications in aerospace, automotive and civil engineering.

This work developed a facile approach to fabricate highly sensitive and flexible polyurethane/graphene platelets composite film for wearable strain sensor. The composite film was fabricated via layer-by-layer laminating method which is simple and cost-effective; it exhibited outstanding electrical conductivity of 1430 ± 50 S/cm and high sensitivity to strain (the gauge factor is up to 150). In the sensor application test, the flexible strain sensor achieves real-time monitoring accurately for five bio-signals such as pulse movement, finger movement, and cheek movement giving a great potential as wearable-sensing device. In addition, the developed strain sensor shows response to pressure and temperature in a certain region. A multifaceted comparison between reported flexible strain sensors and our strain sensor was made highlighting the advantages of the current work in terms of (1) high sensitivity (gauge factor) and flexibility, (2) facile approach of fabrication, and (3) accurate monitoring for body motions.

A novel 2D nanomaterial, Ti ₃ C ₂ T _x MXene, added conductivity and reinforcement to a common elastomer, nitrile butadiene rubber (NBR). X-ray diffraction revealed the intercalation of lithium ions and elastomer chains into the MXene interlayer spacing, which enabled exfoliation in the elastomer. The reaction between MXene and NBR was proved by a stepwise Fourier transform infrared spectroscopy. With increase in MXene fractions, electrical and thermal conductivity of the composite increased to 9 × 10 ⁻⁵ S cm ⁻¹ and 0.69 W m ⁻¹ K ⁻¹ , respectively. At only 2.8 vol% MXene, a swelling ratio of 1.61 was achieved, representing a 75% reduction compared to NBR containing either graphene or carbon nanotubes at the same filler fraction. Tensile tests showed that with the increase in MXene content, Young’s modulus increased while both tensile strength and elongation at break first increased and then decreased. Overall, latex compounding proved to be an efficient technique for forming NBR/MXene nanocomposites. The revealed reaction between MXene and NBR to create functional polymer nanocomposites could provide a platform for utilising MXene for other polymers.