The tactile pressure sensor is of great significance in flexible electronics, but sensitivity customization over the required working range with high linearity still remains a critical challenge. Despite numerous efforts to achieve high sensitivity and a wide working range, most sensitive microstructures tend to be obtained only by inverting naturally existing templates without rational design based on fundamental contact principles or models for piezoresistive pressure sensors. Here, a positive design strategy with a hyperelastic model and a Hertzian contact model for comparison was proposed to develop a flexible pressure sensor with highly customizable linear sensitivity and linearity, in which the microstructure distribution was precalculated according to the desired requirement prior to fabrication. As a proof of concept, three flexible pressure sensors exhibited sensitivities of 0.7, 1.0, and 1.3 kPa⁻¹ over a linear region of up to 200 kPa, with a low sensitivity error (<5%) and high linearity (~0.99), as expected. Based on the superior electromechanical performance of these sensors, potential applications in physiological signal recognition are demonstrated as well, and such a strategy could shed more light on demand-oriented scenarios, including designable working ranges and linear sensitivity for next-generation wearable devices.

Composite membranes have been fabricated made of ultrafine PVDF fibersviaa tip-induced electrospinning (TIE) process and Al₂O₃nanoparticlesviaa dip-coating process.

In this work, the ceramic coating separator (CCS-CS) prepared with polyethylene (PE) separator, Al₂O₃ inorganic particles, carboxymethyl cellulose sodium (CMC) and styrene-butadiene rubber (SBR) mix binders is further modified by coating with a thin polydopamine (PDA) layer through a simple chemical deposition method. Compared with the bare ceramic coating separator, the PDA-modified CCS-CS (CCS-CS-PDA) exhibits excellent thermal stability, which shows no thermal shrinkage after storing at 200 °C for 30 min. Compared with the PE separator, both the uptake and wettability with the electrolyte and water of CCS-CS-PDA are improved significantly. Meanwhile, when saturated with liquid electrolyte, the CCS-CS-PDA also shows enabled high ionic conductance. Furthermore, the test of the electrochemical impedances changing with the temperatures suggests that only the PE separator exhibits no thermal shutdown behaviors, and the CCS-CS separator only has a shutdown temperature range from 138 to 160 °C, while the CCS-CS-PDA shows a shutdown temperature range from 138 to more than 200 °C. The cells prepared with the CCS-CS-PDA also show stable repeated cycling performance and good rate capacity at room temperature.

Remote vascular interventional surgery robotics: a literature review Yang Zhao, Ziyang Mei, Xiaoxiao Luo, Jingsong Mao, Qingliang Zhao, Gang Liu, Dezhi Wu

Ammonia gas sensors are very essential in many industries and everyday life. However, their complicated fabrication process, severe environmental fabrication requirements and desorption of residual ammonia molecules result in high cost and hinder their market acceptance. Here, laser direct writing is used to fabricate three parallel porous 3D graphene lines on a polyimide (PI) tape to simply construct an ammonia gas sensor. The middle one works as an ammonia sensing element and the other two on both sides work as heaters to improve the desorption performance of the sensing element to ammonia gas molecules. The graphene lines were characterized by scanning electron microscopy and Raman spectroscopy. The response and recovery time of the sensor without heating are 214 s and 222 s with a sensitivity of 0.087% ppm⁻¹ for sensing 75 ppm ammonia gas, respectively. The experimental results prove that under the optimized heating temperature of about 70 °C the heaters successfully help implement complete desorption of residual NH₃ showing a good sensitivity and cyclic stability.