The construction industry has a considerable environmental impact in societies, which must be controlled to achieve adequate sustainability levels. In particular, cement production contributes 5–8% of CO₂ emissions worldwide, mainly from the utilization of clinker. This study applied Life Cycle Assessment (LCA) methodology to investigate the environmental impact of cement production and explore environmental improvements obtained by adding marble waste sludges in the manufacture of Portland cement. It was considered that 6–35% of the limestone required for its production could be supplied by marble waste sludge (mainly calcite), meeting the EN 197-1:2011 norm. Energy consumption and greenhouse gas (GHG) emission data were obtained from the Ecovent database using commercial LCA software. All life cycle impact assessment indicators were lower for the proposed “eco-cement” than for conventional cement, attributable to changes in the utilization of limestone and clinker. The most favorable results were achieved when marble waste sludge completely replaced limestone and was added to clinker at 35%. In comparison to conventional Portland cement production, this process reduced GHG emissions by 34%, the use of turbine waters by 60%, and the emission of particles into the atmosphere by 50%. Application of LCA methodology allowed evaluation of the environmental impact and improvements obtained with the production of a type of functional eco-cement. This approach is indispensable for evaluating the environmental benefits of using marble waste sludges in the production of cement.

This study evaluated the waste generated by a Spanish marble-producing company as adsorbent for the removal of copper (Cu [II]) from aqueous media. Six marble waste sludge samples were studied, and the following operational parameters were analyzed in discontinuous regime, including pollutant concentration, pH, temperature, nature of aqueous medium, and ionic strength. The applicability of the adsorbent material was assessed with experiments in both continuous and discontinuous regimes under close-to-real-life conditions. A pseudo-second order model yielded a better fit to the kinetic data. Application of the intraparticle diffusion model revealed two well-differentiated adsorption stages, in which the external material transfer is negligible and intraparticle diffusion is the controlling stage. The equilibrium study was better fitted to a Freundlich-type isotherm, predicting elevated maximum adsorption values (22.7 mg g⁻¹) at a relatively low initial Cu (II) concentration (25 ppm), yielding a highly favorable chemisorption process (n >> 1). X-ray fluorescence study identified calcite (CaCO₃) as the main component of marble waste sludges. According to X-ray diffraction analysis, Cu (II) ion adsorption occurred by intercalation of the metallic cation between CaCO₃ layers and by the formation of surface complexes such as CaCO₃ and Cu₂(CO₃)(OH)₂. Cu (II) was more effectively removed at medium pH, lower temperature, and lower ionic strength of the aqueous medium. The salinity and dissolved organic matter in surface, ground-, and waste-waters negatively affected the Cu (II) removal process in both continuous and discontinuous regimes by competing for active adsorption sites. These findings demonstrate the applicability and effectiveness of marble-derived waste sludges as low-cost and readily available adsorbents for the treatment of waters polluted by Cu (II) under close-to-real-life conditions.