A 2D MoS₂ nanosheet was prepared and treated by sodium dodecyl benzene sulfonate (SDBS) to fabricate 2D MoS₂/SDBS composite (2D-MSC) coating on carbon steel. The anticorrosion performance of coating was comprehensively investigated.

Biofouling poses a significant challenge to the marine industry, and silicone anti-biofouling coatings have garnered extensive attention owing to their environmental friendliness and low surface energy. However, their widespread application is hindered by their low substrate adhesion and weak static antifouling capabilities. In this study, a novel silicone polymer polydimethylsiloxane (PDMS)-based poly(urea-thiourea-imine) (PDMS-PUTI) was synthesized via stepwise reactions of aminopropyl-terminated polydimethylsiloxane (APT-PDMS) with isophorone diisocyanate (IPDI), isophthalaldehyde (IPAL), and carbon disulfide (CS₂). Subsequently, a nanocomposite coating (AgNPs-x/PDMS-PUTI) was prepared by adding silver nanoparticles (AgNPs) to the polymer PDMS-PUTI. The dynamic multiple hydrogen bonds formed between urea and thiourea linkages, along with dynamic imine bonds in the polymer network, endowed the coating with outstanding self-healing properties, enabling complete scratch healing within 10 min at room temperature. Moreover, uniformly dispersed AgNPs not only reduced the surface energy of the coating but also significantly enhanced its antifouling performance. The antibacterial efficiency against common marine bacteria Pseudomonas aeruginosa (P.sp) and Staphylococcus aureus (S.sp) was reduced by 97.08% and 96.71%, respectively, whilst the diatom settlement density on the coating surface was as low as approximately 59 ± 3 diatom cells/mm². This study presents a novel approach to developing high-performance silicone antifouling coatings.

An understanding of the interaction of calcareous deposits and biofoulants on the corrosion performance of steel during the fouling stage is both interesting and necessary. So, the effects of these factors on Q235 carbon steel were investigated and discussed for 20 weeks under real ocean conditions. The results indicate that calcareous deposits are favorable for the attachment of marine microorganisms. However, macroorganisms prefer adhering directly to the substrate. The generations of calcareous deposits have priority over the biofilm attachment under the condition of cathodic protection. Calcareous deposits can prevent steel against corrosion for four weeks without cathodic protection.

Given their outstanding versatile properties, multilayered anticorrosion coatings have drawn great interest from researchers in the academic and engineering fields. However, the application of multilayered coatings is restricted by some limitations such as low interlayer compatibilities, the harsh preparation process, etc. This work introduced a composite film fabricated on a 2A12 aluminum alloy surface, including an anodic oxide film, a sol–gel film, and a layer-by-layer (LBL) self-assembling film from bottom to top. The microstructure and elemental characterization indicated that the finish of the coating with the LBL film resulted in a closely connected multilayered coating with a smoother surface. The anticorrosion performance was systematically evaluated in the simulated corrosive medium and neutral salt spray environment. The integrated coating with the LBL film presented an excellent anticorrosion ability with system impedance over 10⁸ Ω·cm² and a self-corrosion current density two orders of magnitude lower than that of the other coatings. After the acceleration test in a salt spray environment, the multilayered coatings could still show a good protective performance with almost no cracks and no penetration of chloride ions. It is believed that the as-constructed multilayered coating with high corrosive properties and a fine surface state will have promising applications in the field of anticorrosion engineering.