Glass ionomer cement (GIC) is a tailor-made material that is used as a filling material in dentistry. GIC is cured by an acid-base reaction consisting of a glass filler and ionic polymers. When the glass filler and ionic polymers are mixed, ionic bonds of the material itself are formed. In addition, the extra polymer anion reacts with calcium in enamel or dentin to increase adhesion to the tooth tissue. GICs are widely used as adhesives for artificial crowns or orthodontic brackets, and are also used as tooth repair material, cavity liner, and filling materials. In this review, the current status of GIC research and development and its prospects for the future have been discussed in detail.

Hydroxyapatite (HA) is a significant constituent of bones or teeth and is widely used as an artificial bone graft. It is often used to replace the lost bones or in reconstructing alveolar bones before dental implantation. HA with biological functions finds its importance in orthopedic surgery and dentistry to increase the local concentration of calcium ions, which activate the growth and differentiation of mesenchymal stem cells (MSC). To make relevant use of HA in bone transplantation, the surfaces of orthopedic and dental implants are frequently coated with nanosized hydroxyapatite (nHA), but its low dispersibility and tendency to form aggregates, the purpose of the surface modification of bone implants is defeated. To overcome these drawbacks and to improve the histocompatibility of bone implants or to use nHA in therapeutic applications of implants in the treatment of bone diseases, various studies suggested the attachment of biomolecules (growth factors) or drugs through chemical bonding at the surface of nHA. The growth factors or drugs bonded physically at the surface of nHA are mostly unstable and burst released immediately. Therefore, reported studies suggested that the surface of nHA needs to be modified through the chemical bonding of biologically active molecules at the surface of bone implants such as proteins, peptides, or naturally occurring polysaccharides to prevent the aggregation of nHA and to get homogenous dispersion of nHA in solution. The role of irradiation in producing bioactive and antibacterial nHA through morphological variations in surfaces of nHA is also summarized by considering internal structures and the formation of reactive oxygen species on irradiation. This mini-review aims to highlight the importance of small molecules such as proteins, peptides, drugs, and photocatalysts in surface property modification of nHA to achieve stable, bioactive, and antibacterial nHA to act as artificial bone implants (scaffolds) in combination with biodegradable polymers.

To provide a long-term bacterial seal through the formation of reparative dentin bridge, calcium silicate-based pulp capping materials have been used at sites of pulpal exposure. The aim of this study was to evaluate the mineralization-inducing potentials of calcium silicate-based pulp capping materials (ProRoot MTA [PR], Biodentine [BD], and TheraCal LC [TC]) in human dental pulp cells (HDPCs). Specimens of test materials were placed in deionized water for various incubation times to measure the pH variation and the concentration of calcium released. The morphology of HDPCs cultured on the specimens was examined using a confocal laser scanning microscope (CLSM). Alizarin red S staining and alkaline phosphatase assays were used to evaluate mineralization-inducing potentials of the capping materials. BD showed the highest calcium release in all test periods, followed by PR and TC. (p<0.05). All experimental groups showed high alkalinity after 1 day, except at 14 days. BD showed the highest cell viability compared with PR and TC after 1 and 3 days, while TC showed the lowest value (p<0.05). The CLSM analysis showed that cells were well adhered and expressed actin filaments for all pulp capping materials. Mineralization by PR and BD groups was higher than that by TC group based on alizarin red S staining. BD showed significantly higher alkaline phosphatase activity than PR and TC, while TC showed the lowest value (p<0.05). Within the limitations of the in vitro study, BD had higher mineralization-inducing potential than PR and TC.

With recent developments in digital dentistry, research on techniques and materials for three-dimensional (3D) printing is actively underway. We report the clinical applications and outcomes of 3D printing of temporary crowns fabricated with polylactic acid (PLA) using a fused deposition modeling (FDM) printer. Five participants were recruited from among patients scheduled to be treated with a single full-coverage crown at a dental clinic in a university medical center from June to August 2022. We used 3D-printed crowns fabricated with PLA using an FDM printer as temporary crowns and were assessed for discomfort, fracture, and dislodging. The 3D-printed temporary crowns were maintained without fracture, dislodging, or discomfort until the permanent prosthesis was ready. The average time required for printing the temporary crowns was approximately 7 minutes. The 3D printing of temporary crowns with PLA using an FDM printer is a convenient process for dentists. However, these crowns have some limitations, such as rough surface texture and translucency; therefore, the 3D printing process should be improved to produce better prostheses.

Oral mucosal burns can occur after contact with various chemical agents, and commonly manifest as areas of mucosal sloughing and ulceration. Policresulen (Albothyl, Celltrion Pharm Inc.) is an over-the-counter topical antiseptic that is frequently used to treat stomatitis. Policresulen solution is highly acidic, with an approximate pH of 0.6; it can thus cause mucosal injury when improperly applied in the oral cavity. Here, we present a rare case of an oral mucosal burn resulting from incorrect self-administration of policresulen and emphasize the importance of increasing understanding of this adverse drug event among consumers and health professionals.

Background: Residual monomer tests using high-performance liquid chromatography and cytotoxicity tests were performed to analyze the effect on the oral mucosa of a self-curing resin for provisional crown production.Methods: A cytotoxicity test was performed to confirm whether leaked residual monomers directly affected oral mucosal cells. The cytotoxicity of the liquid and solid resin polymers was measured using a water-soluble tetrazolium (WST) test and microplate reader.Results: In the WST assay using a microplate reader, 73.4% of the cells survived at a concentration of 0.2% liquid resin polymer. The cytotoxicity of the liquid resin polymer was low at ≤0.2%. For the solid resins, when 100% of the eluate was used from each specimen, the average cell viability was 91.3% for the solid resin polymer and 100% for the hand-mixed self-curing resin, which is higher than the cell viability standard of 70%. The cytotoxicity of the solid resin polymer was low.Conclusion: Because the polymerization process of the self-curing resin may have harmful effects on the oral mucosa during the second and third stages, the solid resin should be manufactured indirectly using a dental model.