Implementing the concept of mixed construction in modern automotive engineering requires the joining of sheet metal or extruded profiles with cast components made from different materials. As weight reduction is desired, these cast components are usually made from high-strength aluminium alloys of the Al-Si (Mn, Mg) system, which have limited weldability. The mechanical joinability of the cast components depends on their ductility, which is influenced by the microstructure. High-strength cast aluminium alloys have relatively low ductility, which leads to cracking of the joints. This limits the range of applications for cast aluminium alloys. In this study, an aluminium alloy of the Al-Si system AlSi9 is used to investigate relationships between solidification conditions during the sand casting process, microstructure, mechanical properties, and joinability. The demonstrator is a stepped plate with a minimum thickness of 2.0 mm and a maximum thickness of 4.0 mm, whereas the thickness difference between neighbour steps amounts to 0.5 mm. During casting trials, the solidification rates for different plate steps were measured. The microscopic investigations reveal a correlation between solidification rates and microstructure parameters such as secondary dendrite arm spacing. Furthermore, mechanical properties and the mechanical joinability are investigated.

In modern vehicle chassis, multi-material design is implemented to apply the appropriate material for each functionality. In spaceframe technology, both sheet metal and continuous cast are joined to castings at the nodal points of the chassis. Since resistance spot welding is not an option when different materials are joined, research is focusing on mechanical joining methods for multi-material designs. To reduce weight and achieve the required strength, hardenable cast aluminium alloys of the AlSi-system are widely used. Thus, 85–90% of aluminium castings in the automotive industry are comprised of the AlSi-system. Due to the limited weldability, mechanical joining is a suitable process. For this application, various optimisation strategies are required to produce a crack-free joint, as the brittle character of the AlSi alloy poses a challenge. Thus, adapted castings with appropriate ductility are needed. Hence, in this study, the age-hardenable cast aluminium alloy AlSi10Mg is investigated regarding the correlation of the different thicknesses, the microstructural characteristics as well as the resulting mechanical properties. A variation of the thicknesses leads to different solidification rates, which in turn affect the microstructure formation and are decisive for the mechanical properties of the casting as well as the joinability. For the investigation, plates with thicknesses from 2.0 to 4.0 mm, each differing by 0.5 mm, are produced via sand casting. Hence, the overall aim is to evaluate the joinability of AlSi10Mg and derive conclusions concerning the microstructure and mechanical properties.

AlSi casting alloys combine excellent castability with high strength. Hence, this group of alloys is often used in the automotive sector. The challenge for this application is the brittle character of these alloys which leads to cracks during joint formation when mechanical joining technologies are used. A rise in ductility can be achieved by a considerable increase in the solidification rate which results in grain refinement. High solidification rates can be realized in twin–roll casting (TRC) by water‐cooled rolls. Therefore, a hypoeutectic EN AC–AlSi9 (for European Norm ‐ aluminum cast product) is manufactured by the TRC process and analyzed. Subsequently, joining investigations are performed on castings in as‐cast and heat‐treated condition using the self‐piercing riveting process considering the joint formation and the load‐bearing capacity. Due to the fine microstructure, the crack initiation can be avoided during joining, while maintaining the joining parameters, especially by specimens in heat treatment conditions. Furthermore, due to the extremely fine microstructure, the load‐bearing capacity of the joint can be significantly increased in terms of the maximum load‐bearing force and the energy absorbed.

In many manufacturing areas, multi-material designs are implemented in which individual components are joined together to form complex structures with numerous joints. For example, in the automotive sector, cast components are used at the junctions of the body and joined with different types of sheet metal and extruded profiles. To be able to join structures consisting of different materials, alternative joining technologies have emerged in recent years. This includes clinching, which allows assembling of two or more thin sheet metal and casting parts by solely cold forming the material. Clinching the brittle and usually less ductile cast aluminium alloys remains a challenge because the brittle character of the cast aluminium alloys can cause cracks during the forming of the clinched joint. In this study, the influence of the heat treatment time of an aluminium casting alloy AlSi9 on the joinability in the clinching process is investigated. Specific heat treatment of the naturally hard AlSi9 leads to a modification of the eutectic microstructure, which can increase ductility. Based on this, it will be examined if specific clinching die geometries can be used, which achieve an optimized geometrical formation of the clinched joint. The load-bearing capacities of the clinched joints are determined and compared by shear tensile and head tensile tests. Furthermore, the joints are examined microscopically to investigate the influence of the heat treatment on the failure behaviour during the load-bearing tests as well as crack initiation within the joining process.

Multi-material designs (MMD) are more frequently used in the automotive industry. Hereby, the combination of different materials, metal sheets, or cast components, is mechanically joined, often by forming joining processes. The cast components mostly used are high-strength, age-hardenable aluminium alloys of the Al–Si system. Here, the low ductility of the AlSi alloys constitutes a challenge because their brittle nature causes cracks during the joining process. However, by using suitable solidification conditions, it is possible to achieve a microstructure with improved mechanical and joining properties. For this study, we used the twin-roll casting process (TRC) with water-cooled rollers to manufacture the hypoeutectic AlSi10Mg for the first time. Hereby, high solidification rates are realisable, which introduces a microstructure that is about four times finer than in the sand casting process. In particular, it is shown that a fine microstructure close to the modification with Na or Sr is achieved by the high solidification rate in the TRC process without using these elements. Based on this, the mechanical properties increase, and especially the ductility is enhanced. Subsequent joining investigations validate the positive influence of a high solidification rate since cracks in joints can be avoided. Finally, a microstructure-property-joint suitability correlation is presented.

Consistent lightweight construction in the area of vehicle manufacturing requires the increased use of multi-material combinations. This, in turn, requires an adaptation of standard joining techniques. In multi-material combinations, the importance of integral cast components, in particular, is increasing and poses additional technical challenges for the industry. One approach to solve these challenges is adaptable joining elements manufactured by a thermomechanical forming process. By applying an incremental and thermomechanical joining process, it is possible to react immediately and adapt the joining process inline to reduce the number of different joining elements. In the investigation described in this publication, cast plates made of the cast aluminium alloy EN AC-AlSi9 serve as joining partners, which are processed by sand casting. The joining process of hypoeutectic AlSi alloys is challenging as their brittle character leads to cracks in the joint during conventional mechanical joining. To solve this, the frictional heat of the novel joining process applied can provide a finer microstructure in the hypoeutectic AlSi9 cast alloy. In detail, its Si is finer-grained, resulting in higher ductility of the joint. This study reveals the thermomechanical joining suitability of a hypoeutectic cast aluminium alloy in combination with adaptively manufactured auxiliary joining elements.