The silicate-based bioactive glass S53P4 is clinically used in bone regenerative applications in granule form. However, utilization of the glass in scaffold form has been limited by the high tendency of the glass to crystallize during sintering. Here, careful optimization of sintering parameters enabled the manufacture of porous amorphous S53P4 scaffolds with a strength high enough for surgical procedures in bone applications (5 MPa). Sintering was conducted in a laboratory furnace for times ranging from 25 to 300 min at 630 °C, i.e., narrowly below the commencement of the crystallization. The phase composition of the scaffolds was verified with XRD, and the ion release was tested in vitro and compared with granules in continuous flow of Tris buffer and simulated body fluid (SBF). The amorphous, porous S53P4 scaffolds present the possibility of using the glass composition in a wider range of applications.

Sodium-calcium-phosphate based oxynitride glasses and glass-ceramics doped with Mg, Si, and Nb were studied in vitro in simulated body fluid (SBF) under static conditions. The release of ions and pH changes up to 7 days of immersion were investigated. The nitrogen incorporation into phosphate glass matrix was found to notably influence in vitro dissolution only of homogenous glasses. Increasing the nitrogen content in the samples decreased the mean mass loss, while the niobate incorporation increased it. The correlation between the nitrogen content and increase in pH of SBF was also observed. The presence of phosphates crystallites was found to support the dissolution process at the beginning step (up to 3 days).