As medical research progresses, the derivation and development of biological materials such as hydrogels have steadily gained more interest. The biocompatibility and non-toxicity of chitosan make chitosan hydrogels potential carriers for drug delivery. This work aims to develop two multi-reactive, safe, and highly swellable bio-hydrogels consisting of chitosan-graft-glycerol (CS-g-gly) and carboxymethyl chitosan-graft-glycerol (CMCS-g-gly), for sustained and controlled drug release, improved bioavailability along with entrapment in nanocarriers, which reduces side effects of vincristine sulphate. CS-g-gly and CMCS-g-gly are successfully prepared and fully characterized using analytical techniques. Under various conditions, the prepared hydrogels exhibit a high swelling ratio. Vincristine-loaded CS-g-gly (VCR/CS-g-gly), and CMCS-g-gly (VCR/CMCS-g-gly) show high encapsulation efficiency between 72.28-89.97%, and 56.97-71.91%, respectively. VCR/CS-g-gly show a sustained release behavior, and the maximum release of VCR from hydrogels reached 82% after 120 h of incubation. MCF-7 (breast cancer cell line) and MCF-10 (normal breast cell line) are evaluated for cell viability and apoptosis induction. The in-vitro anti-tumor efficacy is investigated using flow cytometry. The tetrazolium-based MTT assay of hydrogels shows no evidence of significant cytotoxicity in MCF-7 and MCF-10 cells. According to these findings, these hydrogels can effectively deliver drugs to MCF-7 and other breast cancer cells.

A hybrid magnetic material γFe₂O₃@Sh@cu₂O was easily prepared from Shilajit (Sh) decorated Fe₃O₄and copper acetate. The prepared magnetic hybrid material was fully characterized using different analysis, including Fourier transform infrared (FT-IR), X-ray diffraction (XRD), inductively coupled plasma (ICP), scanning electron microscopy (SEM), Energy-dispersive X-ray spectroscopy (EDX), X-ray photoelectron spectroscopy (XPS), vibrating sample magnetometer (VSM) thermal gravimetric analysis (TGA) and Brunauer–Emmett–Teller (BET). All these analysis revealed that during coating of Fe₃O₄@Sh using copper salt (II), synchronized redox sorption of Cu^IIto Cu^Ioccurs at the same time as the oxidation of Fe₃O₄to γFe₂O₃. This magnetic catalyst exhibited excellent catalytic activity for regioselective synthesis of 1,4-disubstituted-1,2,3-triazoles via one pot three-component click reaction of sodium azide, terminal alkynes and benzyl halides in the absence of any reducing agent. High yields, short reaction time, high turnover number and frequency (TON = 3.5 * 10⁵and TOF = 1.0 * 10⁶ h⁻¹respectively), easy separation, and efficient recycling of the catalyst are the strengths of the present method.

This work focussed on the synthesis of a new catalytic material isinglass (IG)-based Fe₃O₄@GA@IG core/shell magnetic nanoparticles and the investigation of its catalytic activity in two important multicomponent reactions. Fe₃O₄ nanoparticles were prepared using a simple coprecipitation method and then coated with IG consisting predominantly of the protein collagen in the presence of glutaraldehyde as a cross-linking agent. The obtained hybrid material has been characterized by Fourier transform infrared analysis, scanning electron microscopy, transmission electron microscopy (TEM), vibrating sample magnetometry, energy-dispersive X-ray, X-ray diffraction (XRD), and Brunauer–Emmett–Teller analyses. The results of XRD analysis implied that the prepared nanocomposite consists of two compounds of crystalline magnetite and amorphous IG, and the formation of its core/shell structure had been confirmed by TEM images. The catalytic performance of the as-prepared core/shell bionanocatalyst was evaluated for the first time in the synthesis of 1,4-dihydropyridine and 4H-pyran derivatives under sonication in ethanol. This core/shell structure because of the superparamagnetic property of Fe₃O₄ and unique properties of IG as a bifunctional biocatalyst offers a high potential for many catalytic applications. Recycling study revealed that no significant decrease in the catalytic activity was observed even after six runs.

In the present research, magnetic rhamnolipid-Co/Al layered double hydroxide (MR-LDH) was synthesized to uptake methylene blue (MB) and reactive orange 16 (RO16) from aqueous solution. The main parameters, including pH, adsorbent dosage, contact time, and initial analyte concentration, were optimized to achieve the best adsorption efficiency. Accordingly, the elimination of MB on MR-LDH is improved in the basic medium due to the electrostatic interactions between the negative charge of MR-LDH and the positive charge of MB dye. In contrast, the acidic medium (pH = 3) was favored for RO16 adsorption because of hydrogen bonding between the protonated form of azo dye and protonated hydroxyl groups at the surface of MR-LDH. The calculated maximum adsorption capacities for MB and RO16 were 54.01 and 53.04 mg/g at 313 K, respectively. The Langmuir model, which assumes monolayer adsorption on the adsorbent surface, provides the best explanation for the adsorption of both dyes (R² = 0.9991 for MB and R² = 0.9969 for RO16). Moreover, the pseudo-second-order kinetic model best described the adsorption process for MB (R² = 0.9970) and RO16 (R² = 0.9941). The proposed adsorbent maintains stable adsorption performance for four consecutive cycles. After each adsorption process, MR-LDH is easily separated by an external magnet. The findings show that MR-LDH was found to be an excellent adsorbent for the removal of both cationic and anionic organic dyes from aqueous solutions.