Reinforced concrete (RC) constructions are seriously threatened by chloride-induced corrosion (CIC) and carbonation, which can result in structural degradation, safety issues, and financial losses. Electrochemical methods and microstructural analysis tests are some of the laboratory techniques used to examine key elements of CIC, such as the impact of different variables and the efficacy of mitigation solutions. In situ studies that make use of non-destructive testing, chloride profiling, and half-cell potential measurements offer important new insights into the long-term performance and causes of RC structure deterioration in real-world circumstances. Non-destructive approaches for CIC detection are emerging these days and provide fruitful results. Studies have focused on the use of these approaches for CIC detection on small specimens in the lab as well as on full-scale experiments in the field. This review covers both in situ monitoring and laboratory studies to provide a thorough analysis of CIC.

As a top construction material worldwide, concrete has core weakness relating to low tensile resistance without reinforcement. It is the reason that a variety of innovative materials are being used on concrete to overcome its weaknesses and make it more reliable and sustainable. Further, the embodied carbon of concrete is high because of cement being used as the integral binder. Latest research trends indicate significant potential for carbon fiber as an innovative material for improving concrete mechanical strength. Although significant literature is available on the use of carbon fiber in concrete, a limited number of studies have focused on the utilization of carbon fiber for concrete mechanical strength improvement and the reduction of embodied carbon. Following the gap in research, this study aimed to investigate and optimize the use of carbon fiber for its mechanical characteristics and embodied carbon improvements. The use of carbon fiber in self-compacting concrete lowers sagging. The greatest quantity of carbon fiber is that it reduces the blockage ratio, forcing the concrete to solidify as clumps develop. With time, carbon fiber improves the durability of concrete. Self-compacting concrete with no carbon fiber has a poor tensile strength. Experiments were conducted by adding carbon fiber at 0.2%, 0.4%, 0.6%, 0.8%, and 1.0% by weight. Fresh concrete tests including slump test and L-box test, hardened concrete tests involving compressive strength and splitting tensile strength, and durability tests involving water absorption and acid attack test were conducted. Embodied carbon ratios were calculated for all of the mix ratios and decreasing impact, in the form of eco-strength efficiency, is observed with changes in the addition of carbon fiber in concrete. From the testing results, it is evident that 0.6% carbon fiber is the ideal proportion for increasing compressive strength and split tensile strength by 20.93% and 59%, respectively, over the control mix. Response Surface Methodology (RSM) is then applied to develop a model based on results of extensive experimentation. Optimization of the model is performed and final modelled equations are provided in terms of calculating the impact of addition of carbon fiber in concrete. Positive implications are devised for the development of concrete in the future involving carbon fiber.

Cementitious and recycled materials that have the potential to improve various properties of concrete have attracted the attention of many researchers recently. Different types of cementitious and recycled materials seem to possess certain unique properties to change cement concrete. This experimental study aims to investigate the impact of ground granulated blast furnace slag (GGBFS) and corn cob ash (CCA) as a partial replacement material for Portland cement (PC) and fine aggregate (FA), respectively, on fresh and hardened concrete properties, as well as the embodied carbon of concrete. The concrete mix was blended with 5–20% of GGBFS and 10–40% of corn cob ash, both individually and combined. A total of 300 concrete specimens were made to achieve the targeted strength of 25 MPa at a 0.50 water/cement ratio and cured at 28 days. It is observed that the workability of fresh concrete is lowered as the dosages of GGBFS and CCA increase in the mixture. Moreover, the compressive and split tensile strengths are augmented by 10.94% and 9.15%, respectively, at 10% of GGBFS by the weight of PC at 28 days. Similarly, the compressive and split tensile strengths are augmented by 11.62% and 10.56%, respectively, at 30% of CCA by the weight of FA at 28 days. Moreover, the combined use of 10% of GGBFS as a cementitious ingredient along with 30% of fine aggregate replaced with CCA in concrete provides the highest compressive and splitting tensile strength, with 16.98% and 13.38% at 28 days, respectively. Furthermore, the density and water absorption of concrete were reduced with increasing dosages of GGBFS and FA in concrete at 28 days. In addition, the embodied carbon and energy were also reduced as the replacement content of GGBFS along with CCA increased in concrete. It is concluded that 10% of GGBFS and 30% of CCA are the optimum percentages for structural applications to reduce the use of cement as well as the cost of the project.