The development of low platinum loading hydrogen evolution reaction (HER) catalysts with high activity and stability is of great significance to the practical application of hydrogen energy. This paper reports a simple method to synthesize a highly efficient HER catalyst through coating a highly dispersed PtNi alloy on porous nitrogen-doped carbon (MNC) derived from the zeolite imidazolate skeleton. The catalyst is characterized and analyzed by physical characterization methods, such as XRD, SEM, TEM, BET, XPS, and LSV, EIS, it, v-t, etc. The optimized sample exhibits an overpotential of only 26 mV at a current density of 10 mA cm⁻², outperforming commercial 20 wt% Pt/C (33 mV). The synthesized catalyst shows a relatively fast HER kinetics as evidenced by the small Tafel slope of 21.5 mV dec⁻¹ due to the small charge transfer resistance, the alloying effect between Pt and Ni, and the interaction between PtNi alloy and carrier.

Polypropylene is widely used in the plastics industry, especially in the tobacco industry, served as cigarette filters to reduce tar and harm. However, it’s difficult to degrade these polypropylene plastics and suitable methods for recycling and reuse is urgent. This research proposes an efficient method for the reuse of polypropylene cigarette filters by mixing waste polypropylene filters with nickel source in different proportions, followed by a facile calcination treatment to prepare nickel-modified carbon-based composite materials with microwave absorption properties. Morphology and magnetic properties of as-prepared samples were analyzed via XRD, SEM, and VSM, exhibiting an increase in carbon content with raising nickel content. Nickel ion anchored on polypropylene fiber may facilitate better fixation of carbon chains during the polypropylene decomposition process. Among the as-prepared samples, CN2 exhibited superior microwave absorption performance, with an optimal absorption peak of −26.76 dB at 7.97 GHz when matched with a given thickness of 4.3 mm, and an effective absorption bandwidth of 3.64 GHz (8.04 GHz to 11.68 GHz) with a matching thickness of 3.5 mm, covering the X band. Therefore, the as-prepared microwave absorbers provides a feasible solution for the recycling and reuse of polypropylene filters, aligning with the tobacco industry requirements for sustainable development.