Zeolite X powder was synthesized using natural low-grade diatomite as the main source of Si but only as a partial source of Al via a simple and green hydrothermal method. The microstructure and surface properties of the obtained samples were characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), wavelength dispersive X-ray fluorescence (XRF), calcium ion exchange capacity (CEC), thermogravimetric-differential thermal (TG-DTA) analysis, and N₂ adsorption-desorption technique. The influence of various synthesis factors, including aging time and temperature, crystallization time and temperature, Na₂O/SiO₂ and H₂O/Na₂O ratio on the CEC of zeolite, were systematically investigated. The as-synthesized zeolite X with binary meso-microporous structure possessed remarkable thermal stability, high calcium ion exchange capacity of 248 mg/g and large surface area of 453 m²/g. In addition, the calcium ion exchange capacity of zeolite X was found to be mainly determined by the crystallization degree. In conclusion, the synthesized zeolite X using diatomite as a cost-effective raw material in this study has great potential for industrial application such as catalyst support and adsorbent.

Porous graphitic carbon nitride (g-C₃N₄) was prepared by dicyandiamide and urea via the pyrolysis method, which possessed enhanced visible-light-driven photocatalytic performance. Its surface area was increased from 17.12 to 48.00 m²/g. The porous structure not only enhanced the light capture capacity, but also accelerated the mass transfer ability. The Di (Dicyandiamide)/Ur (Urea) composite possessed better photocatalytic activity for Rhodamine B in visible light than that of g-C₃N₄. Moreover, the Di/Ur-4:5 composite showed the best photoactivity, which was almost 5.8 times that of g-C₃N₄. The enhanced photocatalytic activity showed that holes and superoxide radical played a key role in the process of photodegradation, which was ascribed to the enhanced separation of photogenerated carriers. The efficient separation of photogenerated electron-hole pairs may be owing to the higher surface area, O dopant, and pore volumes, which can not only improve the trapping opportunities of charge carriers but also the retarded charge carrier recombination. Therefore, it is expected that the composite would be a promising candidate material for organic pollutant degradation.

Diatomite-based X zeolite was obtained and its crystallinity, morphology, and interface properties were investigated by XRD, BET, SEM, EDS, and XRF. The obtained X zeolite possessed a unique meso-microporous structure and showed good ion exchange properties for Cu²⁺ and Zn²⁺. The pseudo-second-order model and Langmuir isotherm model can best describe the adsorption kinetics and isotherms of Cu²⁺ and Zn²⁺, respectively. The maximal adsorption capacities of X zeolite for Cu²⁺ and Zn²⁺ were 146 and 195 mg/g at 323 K, respectively. Meanwhile, the adsorption process for Cu²⁺ and Zn²⁺ were chemical adsorption and ion exchange, respectively. Furthermore, the adsorption data turned out to be an endothermic and spontaneous process. Compared with other reported materials, the adsorption capacity of X zeolite synthesized from diatomite was among the highest. Therefore, it could be a promising adsorbent for the disposal of wastewater that contains metal ions.