Graphene quantum dots (GQDs) with their edge-bound nanometer-size present distinctive properties owing to quantum confinement and edge effects. We report a facile ultrasonic approach with chemical activation using KOH to prepare activated GQDs or aGQDs enriched with both free and bound edges. Compared to GQDs, the aGQDs we synthesized had enhanced BET surface area by a factor of about six, the photoluminescence intensity by about four and half times and electro-capacitance by a factor of about two. Unlike their non-activated counterparts, the aGQDs having enhanced edge states emit enhanced intense blue luminescence and exhibit electrochemical double layer capacitance greater than that of graphene, activated or not. Apart from their use as part of electrodes in a supercapacitor, the superior luminescence of aGQDs holds potential for use in biomedical imaging and related optoelectronic applications.

TiO2 nanofibers (30–50 nm diameter), fabricated by the electro-spinning process, were modified with organo-silane agents via a coupling reaction and were grafted with carbohydrate molecules. The mixture was carbonized to produce a uniform coating of amorphous carbon on the surface of the TiO2 nanofibers. The TiO2@C nanofibers were characterized by high resolution electron microscopy (HRTEM), x-ray diffraction (XRD), x-ray photoelectron (XPS), Fourier transform infrared (FTIR) and UV-vis spectroscopy. The photocatalytic property of the functional TiO2 and carbon nanocomposite was tested via the decomposition of an organic pollutant. The catalytic activity of the covalently functionalized nanocomposite was found to be significantly enhanced in comparison to unfunctionalized composite and pristine TiO2 due to the synergistic effect of nanostructured TiO2 and amorphous carbon bound via covalent bonds. The improvement in performance is due to bandgap modification in the 1D co-axial nanostructure where the anatase phase is bound by nano-carbon, providing a large surface to volume ratio within a confined space. The superior photocatalytic performance and recyclability of 1D TiO2@C nanofiber composites for water purification were established through dye degradation experiments.