In this study, we report a low cost, fast and unexplored electrochemical synthesis strategy of copper oxide nanoneedles films as well as their morphological and chemical characterization. The nanostructured films were prepared using electrochemical anodization in alkaline electrolyte solutions of ethylene glycol, water and fluoride ions. The film morphology shows nanoneedle-shaped structures, with lengths up to 1–2 μm; meanwhile, high-resolution X-ray photoelectron spectroscopy (HRXPS) and spectroscopy Raman analyses indicate that a mixture of Cu(II) and Cu(I) oxides, or only Cu(I) oxide, is obtained as the percentage of water in the electrolyte solution decreases. A preliminary study was also carried out for the photocatalytic degradation of the methylene blue (MB) dye under irradiation with simulated sunlight in the presence of the nanoneedles obtained, presenting a maximum degradation value of 88% of MB and, thus, demonstrating the potential characteristics of the material investigated in the degradation of organic dyes.

This work reports the synthesis and characterization of a novel rhenium(I) complex incorporating a phosphorus–nitrogen (P,N) ligand. The compound crystallizes in a distorted octahedral geometry, as confirmed by single-crystal X-ray diffraction analysis. The complexes were evaluated as catalysts in the transfer hydrogenation of acetophenone using 2-propanol as the hydrogen source. Comparative studies with other rhenium(I) complexes bearing polypyridine ligands revealed high catalytic performance, achieving conversions between 68% and 99%. These results highlight the promising potential of P,N-ligand rhenium complexes in homogeneous transfer hydrogenation catalysis. The optimal reaction time was found to be 4 h for the complexes studied, with only the fac-[Re(CO)₃(PN)Cl] complex showing improved conversion upon extending the reaction time to 7 h, likely due to the donor effects provided by the P,N-ligand.