Interfaces in heterostructures of crystalline materials could strongly affect the slip of dislocations. Such interfaces have become one of the most popular methods to tailor material strength and ductility. This review focuses on the interaction of dislocations and interfaces in heterostructures, in which at least one component is metallic, as investigated by molecular dynamics, in order to systematically summarize our understanding about how dislocations interact with the interfaces. All the possible heterostructures of metallic materials are covered, such as twin boundaries, grain boundaries, bi-metal interfaces and metal/non-metal interfaces. Dislocations may either penetrate the interfaces by inducing steps into the interfaces or dissociate within the interfaces, depending on the type and orientation of the interface as well as the applied strain. Related dislocation interactions at the interface are also presented. In addition, we also discuss the effect of dislocation types, of applied strain and of the deformation method on the interaction of dislocations and interfaces.

The recrystallization and intergranular corrosion behaviors impacted by the additions of Sc and Zr in Al-Zn-Mg-Cu alloys are investigated. The stronger effect of coherent Al₃(Sc_1−xZr_x) phases on pinning dislocation resulted in a lower degree of recrystallization in Al-Zn-Mg-Cu-Sc-Zr alloy, while the subgrain boundaries can escape from the pinning of Al₃Zr phases and merge with each other, bringing about a higher degree of recrystallization in Al-Zn-Mg-Cu-Zr alloy. A low degree of recrystallization promotes the precipitation of grain boundary precipitates (GBPs) with a discontinuous distribution, contributing to the high corrosion resistance of Al-Zn-Mg-Cu-Sc-Zr alloy in the central layer. The primary Al₃(Sc_1−xZr_x) phase promotes recrystallization due to particle-stimulated nucleation (PSN), and acts as the cathode to stimulate an accelerated electrochemical process between the primary Al₃(Sc_1−xZr_x) particles and GBPs, resulting in a sharp decrease of the corrosion resistance in the surface layer of Al-Zn-Mg-Cu-Sc-Zr alloy.

Under compressive testing at 400 °C and a strain rate range of 0.05–5 s⁻¹, the hot deformation behavior and microstructure evolution of an as-cast (AC), as-extruded (with a bimodal grain structure (named as Ex-1) or a relatively uniform fine grain structure (Ex-2)) WE43 alloy have been investigated and compared. The results indicate that the AC sample exhibits the highest peak stress, while the Ex-2 sample has the lowest value. Within the AC material, fine grains were firstly formed along the pancake-like deformed grains (as a necklace structure). The necklace structure was also formed within the Ex-1 and Ex-2 materials at high strain rates of 0.5 and 5 s⁻¹. However, a lamellar structure that the coarse elongated grains divided by parallel boundaries was formed within the Ex-1 material. A relatively more homogeneous fine grain structure is achieved after a true strain of 1.0 within the Ex-2 material at a low strain rate of 0.05 s⁻¹. In addition, a discontinuous dynamic recrystallization mechanism by grain boundary bulging is found to occur. After a true strain of 1.2, a (0001) fiber texture, a typical rare earth (RE) texture, and a relatively random texture are formed within the AC, Ex-1, and Ex-2 WE43 alloy material, respectively.