The aims of this work were to determine the color change and physical–mechanical properties of polystyrene glulam from three tropical wood species. Wood laminas were cut from logs harvested from a young plantation forest of manii (Maesopsis eminii), mangium (Acacia mangium), and rubber-wood (Hevea brasiliensis). The laminas were impregnated with monomer styrene that was polymerized using potassium peroxy-disulfate as a catalyst and heat. Three-layer glulam was constructed from the polystyrene laminas, using isocyanate glue and cold press. For comparison purposes, three-layer untreated glulam and solid wood samples were prepared. The results showed that the color change of polystyrene glulam was very small compared with untreated glulam. Polystyrene glulam had the highest density, while the density of untreated glulam did not differ from that of the solid wood. The moisture content of all products was matched to the environment, and fulfilled the Japanese standard. Compared with both types of glulams, solid wood had lower values for modulus of rupture (MOR), modulus of elasticity (MOE), and hardness, but higher shear strength. Meanwhile, polystyrene glulam had lower values for MOR and MOE, equal shear strength and wood failure, and higher hardness than the untreated glulam. All glulams had very little delamination in the hot water test. Only rubber-wood glulams fulfilled JAS 234-2003 for MOR, MOE, shear strength, and delamination. To obtain adequate physical–mechanical properties of glulams, medium-density wood is recommended for glulam manufacturing.

Laboratory-made particleboards were tested for their resistance to subterranean termite, Coptotermes curvignathus Holmgren (Order Isoptera, Family Termitidae) by Indonesian standard SNI 01.7207–2006, during four weeks and at the end of the test their mass loss percentage and feeding rate were determined. Particleboards consisted of: jabon (Anthocephalus cadamba, Family Rubiacea) with a density of 0.41 g/cm³; sungkai (Peronema canescens, Family Verbenaceae) with a density of 0.46 g/cm³; mangium (Acacia mangium, Family Rhamnaceae) with a density of 0.60 g/cm³ separately and the three species mixture at a rate of 1:1:1. Densities of the boards were targetted at 0.60 g/cm³ and 0.80 g/cm³ by using 12% urea formaldehyde as binder with 2% paraffin as additive based on oven dry wood particle weight. The hand-formed mats and hot-pressing at 130 °C and 2.45 MPa for 10 min were applied. The results showed that particleboards density did not affect mass loss and feeding rate, but the particleboards made from higher density wood resulted in higher resistance to subterranean termite attack. The most resistant particleboards were made of magium, followed by sungkai, mixed species, and jabon.