Microbe-mediated precipitation of Mn-oxides enriched in rare earth elements (REE) and other trace elements was discovered in tunnels leading to the main shaft of the Ytterby mine, Sweden. Defining the spatial distribution of microorganisms and elements in this ecosystem provide a better understanding of specific niches and parameters driving the emergence of these communities and associated mineral precipitates. Along with elemental analyses, high-throughput sequencing of the following four subsystems were conducted: (i) water seeping from a rock fracture into the tunnel, (ii) Mn-oxides and associated biofilm; referred to as the Ytterby Black Substance (YBS) biofilm (iii) biofilm forming bubbles on the Mn-oxides; referred to as the bubble biofilm and (iv) fracture water that has passed through the biofilms. Each subsystem hosts a specific collection of microorganisms. Differentially abundant bacteria in the YBS biofilm were identified within the Rhizobiales (e.g. Pedomicrobium), PLTA13 Gammaproteobacteria, Pirellulaceae, Hyphomonadaceae, Blastocatellia and Nitrospira. These taxa, likely driving the Mn-oxide production, were not detected in the fracture water. This biofilm binds Mn, REE and other trace elements in an efficient, dynamic process, as indicated by substantial depletion of these metals from the fracture water as it passes through the Mn deposit zone. Microbe-mediated oxidation of Mn(II) and formation of Mn(III/IV)-oxides can thus have considerable local environmental impact by removing metals from aquatic environments.

Manganese oxides occur in a wide range of environmental settings either as coatings on rocks, sediment, and soil particles, or as discrete grains. Although the production of biologically mediated Mn oxides is well established, relatively little is known about microbial-specific strategies for utilizing Mn in the environment and how these affect the morphology, structure, and chemistry of associated mineralizations. Defining such strategies and characterizing the associated mineral properties would contribute to a better understanding of their impact on the local environment and possibly facilitate evaluation of biogenicity in recent and past Mn accumulations. Here, we supplement field data from a Mn rock wall deposit in the Ytterby mine, Sweden, with data retrieved from culturing Mn oxidizers isolated from this site. Microscopic and spectroscopic techniques are used to characterize field site products and Mn precipitates generated by four isolated bacteria (Hydrogenophaga sp., Pedobacter sp., Rhizobium sp., and Nevskia sp.) and one fungal-bacterial co-culture (Cladosporium sp.—Hydrogenophaga sp. Rhizobium sp.—Nevskia sp.). Two of the isolates (Pedobacter sp. and Nevskia sp.) are previously unknown Mn oxidizers. At the field site, the onset of Mn oxide mineralization typically occurs in areas associated with globular wad-like particles and microbial traces. The particles serve as building blocks in the majority of the microstructures, either forming the base for further growth into laminated dendrites-botryoids or added as components to an existing structure. The most common nanoscale structures are networks of Mn oxide sheets structurally related to birnessite. The sheets are typically constructed of very few layers and elongated along the octahedral chains. In places, the sheets bend and curl under to give a scroll-like appearance. Culturing experiments show that growth conditions (biofilm or planktonic) affect the ability to oxidize Mn and that taxonomic affiliation influences crystallite size, structure, and average oxidation state as well as the onset location of Mn precipitation.

The dominant initial phase formed during microbially mediated manganese oxidation is a poorly crystalline birnessite-type phyllomanganate. The occurrence of manganese deposits containing this mineral is of interest for increased understanding of microbial involvement in the manganese cycle. A culture independent molecular approach is used as a first step to investigate the role of microorganisms in forming rare earth element enriched birnessite-type manganese oxides, associated with water bearing rock fractures in a tunnel of the Ytterby mine, Sweden. 16S rRNA gene results show that the chemotrophic bacterial communities are diverse and include a high percentage of uncultured unclassified bacteria while archaeal diversity is low with Thaumarchaeota almost exclusively dominating the population. Ytterby clones are frequently most similar to clones isolated from subsurface environments, low temperature milieus and/or settings rich in metals. Overall, bacteria are dominant compared to archaea. Both bacterial and archaeal abundances are up to four orders of magnitude higher in manganese samples than in fracture water. Potential players in the manganese cycling are mainly found within the ferromanganese genera Hyphomicrobium and Pedomicrobium, and a group of Bacteroidetes sequences that cluster within an uncultured novel genus most closely related to the Terrimonas. This study strongly suggest that the production of the YBS deposit is microbially mediated.

Microbial mats or biofilms are known to colonize a wide range of substrates in aquatic environments. These dense benthic communities efficiently recycle nutrients and often exhibit high tolerance to environmental stressors, characteristics that enable them to inhabit harsh ecological niches. In some special cases, floating biofilms form at the air-water interface residing on top of a hydrophobic microlayer. Here, we describe biofilms that reside at the air-air interface by forming gas bubbles (bubble biofilms) in the former Ytterby mine, Sweden. The bubbles are built by micrometer thick membrane-like biofilm that holds enough water to sustain microbial activity. Molecular identification shows that the biofilm communities are dominated by the neuston bacterium Nevskia. Gas bubbles contain mostly air with a slightly elevated concentration of carbon dioxide. Biofilm formation and development was monitored in situ using a time-lapse camera over one year, taking one image every second hour. The bubbles were stable over long periods of time (weeks, even months) and gas build-up occurred in pulses as if the bedrock suddenly exhaled. The result was however not a passive inflation of a dying biofilm becoming more fragile with time (as a result of overstretching of the organic material). To the contrary, microbial growth lead to a more robust, hydrophobic bubble biofilm that kept the bubbles inflated for extended periods (several weeks, and in some cases even months).

A black substance exuding from fractures was observed in 2012 in Ytterby mine, Sweden, and identified in 2017 as birnessite with the composition M_x[Mn(III,IV)]₂O₄∙(H₂O)_n. M is usually calcium and sodium, with x around 0.5. The Ytterby birnessite is unique, with M being calcium, magnesium, and also rare earth elements (REEs) constituting up to 2% of the total metal content. The biogenic origin of the birnessite was established in 2018. Analysis of the microbial processes leading to the birnessite formation and the REE enrichment has continued since then. The process is fast and dynamic, as indicated by the depletion of manganese and of REE and other metals in the fracture water during the passage over the precipitation zone in the mine tunnel. Studies of the exchangeability of metals in the structure are the main objective of the present program. Exposure to solutions of sodium, calcium, lanthanum, and iron led to exchanges and altered distribution of the metals in the birnessite, however, generating phases with almost identical structures after the exchanges, and no new mineral phases were detected. Exchangeability was more efficient for trivalent elements (REE) over divalent (calcium) and monovalent (sodium) elements of a similar size (ionic radii 90–100 pm).