CrNbTaVW_x with (x = 1 and 1.7) high entropy alloys have been devised for thermal barriers between the plasma-facing tungsten tiles and the copper-based heat sink in the first wall of fusion nuclear reactors. These novel materials were prepared by ball milling and consolidated by Upgrade Field Assisted Sintering Technology at 1873 K under an applied pressure of 90 MPa for 10 min. In this work, the structural and mechanical properties of these materials were evaluated. Consolidated samples presented a major phase with a bcc-type structure with lattice parameter value of 0.316 nm for CrNbTaVW and CrNbTaVW_1.7 compositions. Moreover, observation of the microstructures evidences also two minor phases: Ta-Nb-Cr and Ta-V rich (in which carbon is detected). Despite the similarity in the structural properties of these two alloys, their mechanical properties are distinct. The flexural stress for the sample with higher amount of W (CrNbTaVW_1.7) is higher by 50% in the 298–873 K range, with an increased strain to fracture, which can be associated with reduced brittleness caused by the additional W incorporation.