Alkali-activated cement (AAC) is a promising binder that replaces ordinary Portland cement (OPC). In this study, the development of setting time and strength of AAC mixes were studied using ultrasonic testing method. The test results were compared with traditional Vicat setting time and compressive and flexural strengths. The findings showed that setting times and strengths have a strong correlation with ultrasonic velocity curve. The initial setting time corresponds well with the ultrasonic velocity curve’s dormant period, and the final setting time with the time it takes to reach the velocity curve’s maximum acceleration. Both setting times also showed a correlation with the value of the maximum acceleration. An exponential relation was found between the ultrasonic velocity and the compressive and flexural strengths. The effect of binder content, alkaline solid to binder ratio (AS/B), sodium silicate to sodium hydroxide solids ratio (SS/SH), and total water to total solid binder ratio (TW/TS) on the strength and setting time are also studied using Taguchi method of experimental design. AS/B ratio showed a significant influence on the setting time of AAC while TW/TS ratio showed only a minor effect. The ultrasonic velocities were able to capture the effect of the different parameters similar to the compressive strength. The velocity decreased mainly with the increase of TW/TS ratio and binder content, while AS/B and SS/SH ratios showed a lower influence.

The paper investigates the freeze–thaw resistance and sorptivity behavior of fine‐grained alkali‐activated concrete cured at ambient temperature. A blended binder system containing fly ash, ground granulated blast furnace slag, and silica fume was used. A combination of sodium hydroxide and sodium silicate was used as an activator. The freeze–thaw resistance was evaluated based on mass loss (scaling), and the extent of internal damage was assessed by testing the ultrasonic time at different cycles. Initial and secondary sorptivity coefficients were calculated based on the cumulative water absorption values at different time intervals. Alkali content, sodium silicate to sodium hydroxide ratio, and water to binder ratio were investigated. The experimental results showed that water to binder ratio is the most significant parameter for the scaling; higher ratios result in higher scaling. In terms of internal damage, alkali content is the most significant. The increase of alkali increased the amount of internal damage in the concrete. The initial sorptivity coefficient increased with the water and alkali content and decreased with the silicate content. The secondary sorptivity coefficient showed no significant change with the investigated parameters.

Alkali-activated cement (AAC) is an alternative cement that has been increasingly studied over the past decades mainly because of its environmental benefits. However, most studies are on heat-cured AACs and are focused on mechanical properties. There is a lack of research on the fresh properties of ambient-cured AAC systems. This study investigates the rheological properties of ambient-temperature-cured alkali-activated blended binder mixtures activated with sodium silicate and sodium hydroxide solutions. The influence of binder amount, alkaline solid to binder ratio (AS/B), sodium silicate to sodium hydroxide solids ratio (SS/SH), and total water content to total solid (from the binding materials) ratio (TW/TS) on the rheological properties are investigated. The effect of borax as an admixture and silica fume as a replacement for fly ash is also investigated. The results showed that both the yield stress and plastic viscosity are mainly affected by the binder content and TW/TS ratio decreasing with the increase of each parameter. The yield stress increased with the increase of the SS/SH ratio. Borax significantly reduced the yield stress, while silica fume’s effect was dependent on its dosage.