Spinodal decomposition is discovered to be an effective way to strengthen magnesium alloy.

Body-centred cubic magnesium-lithium-aluminium-base alloys are the lightest of all the structural alloys, with recently developed alloy compositions showing a unique multi-dimensional property profile. By hitherto unrecognised mechanisms, such alloys also exhibit exceptional immediate strengthening after solution treatment and water quenching, but strength eventually decreases during prolonged low temperature ageing. We show that such phenomena are due to the precipitation of semi-coherent D0₃-Mg₃Al nanoparticles during rapid cooling followed by gradual coarsening and subsequent loss of coherency. Physical explanation of these phenomena allowed the creation of an exceptionally low-density alloy that is also structurally stable by controlling the lattice mismatch and volume fraction of the Mg₃Al nanoparticles. The outcome is one of highest specific-strength engineering alloys ever developed.

N -type β-FeSi2/p-type Si heterojunctions were fabricated from β-FeSi2 films epitaxially grown on Si(111) by facing-target direct-current sputtering. Sharp film-substrate interfaces were confirmed by scanning electron microscopy. The current-voltage and photoresponse characteristics were measured at room temperature. They exhibited good rectifying properties and a change of approximately one order of magnitude in the current at a bias voltage of −1 V under illumination by a 6 mW, 1.31 μm laser. The estimated detectivity was 1.5×109 cm √Hz W at 1.31 μm. The results suggest that the β-FeSi2/Si heterojunctions can be used as near-infrared photodetectors that are compatible with silicon integrated circuits.