New stable nanocomposites with copper nanoparticles (CuNPs) in a polymer matrix have been synthesized by green chemistry. Non-toxic poly-N-vinylimidazole was used as a stabilizing polymer matrix and ascorbic acid was used as a reducing agent. The polymer CuNPs nanocomposites were characterized by Fourier transform infrared (FTIR) spectroscopy, ultraviolet–visible (UV) spectroscopy, transmission electron microscopy (TEM), scanning electron microscopy (SEM), atomic absorption spectroscopy (AAS), and thermogravimetric analysis (TGA). It was shown, using the dynamic light scattering (DLS) method, that the hydrodynamic diameters of nanocomposites depend on the CuNPs content and are in an associated state in an aqueous medium. The copper content in nanocomposites ranges from 1.8 to 12.3% wt. The obtained polymer nanocomposites consist of isolated copper nanoparticles with a diameter of 2 to 20 nm with a spherical shape.

An insoluble nanocomposite with copper nanoparticles (CuNP) stabilized by 1-vinyl-1,2,4-triazole and acrylonitrile copolymer was synthesized and characterized by scanning electron microscopy, Fourier transform infrared spectroscopy, X-ray diffraction, and thermogravimetric data analysis. The nanocomposite showed high catalytic activity in the multicomponent synthesis of 1-benzyl-4-phenyl- and 1-benzyl-4-phenyl-5-(2-phenylethynyl)-1H-1,2,3-triazoles.

A new hydrophilic polymeric nanocomposite containing AgNPs was synthesized by chemical reduction of metal ions in an aqueous medium in the presence of the copolymer. A new water-soluble copolymer of 1-vinyl-1,2,4-triazole and vinylsulfonic acid sodium salt (poly(VT-co-Na-VSA)) was obtained by free-radical copolymerization and was used as a stabilizing precursor agent. The structural, dimensional, and morphological properties of the nanocomposite were studied by UV–Vis, FTIR, X-ray diffraction, atomic absorption, transmission and scanning electron microscopy, dynamic and electrophoretic light scattering, gel permeation chromatography, thermogravimetric analysis, and differential scanning calorimetry. Hydrodynamic diameter of macroclubs for the copolymer was 171 nm, and for the nanocomposite it was 694 nm. Zeta potential for the copolymer was −63.8 mV, and for the nanocomposite it was −70.4 mV. The nanocomposite had strong antimicrobial activity towards Gram-negative and Gram-positive microorganisms: MIC and MBC values were in the range of 0.25–4.0 and 0.5–8.0 μg/mL, respectively.

Reaction of tetrafluorosilane with tris(2-hydroxyethyl)-and tris(2-trimethylsiloxyethyl)amine results in formation of 1-fluorosilatrane and fluorosilatrane in 75 and 53% yield, respectively. Reaction of tetrafluorosilane with bis(2-trimethylsiloxyethyl)amine and its N-methyl derivative leads to the hitherto unknown 1,1-difluoroquasisilatranes (N → Si) F₂Si(OCH₂CH₂)₂NR (R = H, Me) containing donor-acceptor bond N → Si and pentacoordinate silicon atom. The structure of the synthesized compounds was proved by ¹H, ¹³C, ¹⁵N, ¹⁹F, ²⁹Si NMR and IR spectroscopy.