Coating building envelopes with a passive daytime radiative cooling (PDRC) material has attracted enormous attention as an alternative cooling technique with minimal energy consumption and carbon footprint. Despite the exceptional performance and scalability of porous polymer coating (PPC), achieving consistent performance over a wide range of drying environments remains a major challenge for its commercialization as a radiative cooling paint. Herein, we demonstrate the humidity vulnerability of PPC during the drying process and propose a simple strategy to greatly mitigate the issue. Specifically, we find that the solar reflectance of the PPC rapidly decreases with increasing humidity from 30% RH, and the PPC completely losses its PDRC ability at 45% RH and even become a solar-heating material at higher humidity. However, by adding a small amount of polymer reinforcement to the PPC, it maintains its PDRC performance up to 60% RH, resulting in a 950% increase in estimated areal coverage compared to PPC in the United States. This study sheds light on a crucial consistency issue that has thus far been rarely addressed, and offers engineering guidance to handle this fundamental threat to the development of dependable PDRC paint for industrial applications.

Here, we investigate a wearable-based IR and thermal stealth structure that effectively blocks IR and thermal radiation from a human body or device using a polyurethane–antimony tin oxide (PU–ATO) composite fiber. The aging time of the ATO sol prepared by a sol–gel method, and the concentration of ATO with respect to that of the PU matrix were optimized to prepare PU–ATO composite fibers that simultaneously have an appropriate mechanical strength (strength of ~4 MPa and strain of ~340%) and IR- and thermal radiation-shielding properties with ~98% IR light, as determined by Fourier transform IR spectroscopic studies. The fabricated PU–ATO composite fiber showed stable IR- and thermal radiation-shielding properties even when exposed to ten cycles of repeated temperature changes of −20 and +80 °C and long-term temperature changes for 30 days. In addition, the surface of the PU–ATO composite fiber was rendered hydrophobic to prevent the distortion of the IR and thermal radiation due to the wetting of the PU–ATO composite fiber with absorbed water. The PU–ATO composite fiber-based textile proposed herein can be applied in wearable IR- and thermal radiation-shielding technologies to shield IR signals generated by objects of diverse and complex shapes.

Surface plasmon resonance (SPR) sensors based on a silver film suffer from signal degradation due to silver oxidation in aqueous sensing environments. To overcome this limitation, we fabricated the planar plasmonic substrate employing an atomic MoS₂ layer on a silver surface. Successful production of a large-area MoS₂ monolayer blocks the penetration of oxygen and water molecules. In addition, we theoretically and experimentally found that MoS₂ layer on the silver film can improve the SPR sensitivity and stability significantly. In this study, the proposed SPR substrate has the potential to provide highly enhanced sensor platforms for surface-limited molecular detections.