Despite being first demonstrated over 160 years ago, and offering significant environmental benefits and high electrical efficiency, it is only in the last two decades that fuel cells have offered a realistic prospect of being commercially viable. The solid oxide fuel cell (SOFC) offers great promise and is presently the subject of intense research activity. Unlike other fuel cells the SOFC is a solid-state device which operates at elevated temperatures. This review discusses the particular issues facing the development of a high temperature solid-state fuel cell and the inorganic materials currently used and under investigation for such cells, together with the problems associated with operating SOFCs on practical hydrocarbon fuels.

Numerous investigations have been carried out into the conversion of biogas into synthesis gas (a mixture of H₂ + CO) over Ni/YSZ anode cermet catalysts. Biogas is a variable mixture of gases consisting predominantly of methane and carbon dioxide (usually in a 2 : 1 ratio, but variable with source), with other constituents including sulfur-containing gases such as hydrogen sulfide, which can cause sulfur poisoning of nickel catalysts. The effect of temperature on carbon deposition and sulfur poisoning of 90 : 10 mol% Ni/YSZ under biogas conversion conditions has been investigated by carrying out a series of catalytic reactions of methane-rich (2 : 1) CH₄ /CO₂ mixtures in the absence and presence of H₂S over the temperature range 750–1000 °C. The effect of ceria-doping on carbon dioxide reforming, carbon deposition and sulfur tolerance has also been investigated by carrying out a similar series of reactions over ceria-doped Ni/YSZ. Ceria was doped at 5 mol% of the nickel content to give an anode catalyst composition of 85.5 : 4.5 : 10 mol% Ni/CeO₂ /YSZ. Reactions were followed using quadrupolar mass spectrometry (QMS) and the amount of carbon deposition was analysed by subjecting the reacted catalyst samples to a post-reaction temperature programmed oxidation (TPO). On undoped Ni/YSZ, carbon deposition occurred predominantly through thermal decomposition of methane. Ceria-doping significantly suppressed methane decomposition and at high temperatures simultaneously promoted the reverse Boudouard reaction, significantly lowering carbon deposition. Sulfur poisoning of Ni/YSZ occurred in two phases, the first of which caused the most activity loss and was accelerated on increasing the reaction temperature, while the second phase had greater stability and became more favourable with increasing reaction temperature. Adding H₂S significantly inhibited methane decomposition, resulting in much less carbon deposition. Ceria-doping significantly increased the sulfur tolerance of Ni/YSZ, however, in the presence of H₂S ceria did not promote the reverse Boudouard reaction and at high temperatures carbon deposition was greater over ceria-doped Ni/YSZ. In order to further study the effects of ceria-doping, a solid oxide fuel cell (SOFC) was constructed with a ceria-doped anode cermet and its electrical performance on simulated biogas compared to hydrogen was tested. This fuel cell was subsequently ran for 1000 h on simulated biogas with no degradation in its overall electrical performance.

In this paper we describe the use of a perovskite material synthesised by a low temperature route for the conversion of methane-rich biogas into synthesis gas, which shows high activity and selectivity and extremely good resistance to deleterious carbon deposition.

The use of CO₂ in reforming methane to produce the industrial feedstock syngas is an economically and environmentally attractive reaction. An alumina-supported nickel catalyst active for this reaction additionally forms filamentous carbon. The catalyst is investigated by inelastic neutron scattering as well as elemental analysis, temperature-programmed oxidation, temperature-programmed hydrogenation, X-ray diffraction, transmission electron microscopy and Raman scattering. Isotopic substitution experiments, using ¹³CO₂ for ¹²CO₂, show the oxidant to contribute to the carbon retention evident with this sample. At steady-state operation, a carbon mass balance of 95% is observed. A kinetic scheme is proposed to account for the trends observed.