Gamma-alumina nanoparticles (γANPs) were obtained from a low-cost process by using natural bauxites. The γANPs materials were characterized by X-ray powder diffraction (XRPD), Fourier-transform infrared spectroscopy (FTIR), Brunauer–Emmett–Teller (BET) theory, scanning electron microscopy (SEM), atomic force microscopy (AFM), and were functionalized with N-cetyl-N, N, N, trimethylammonium bromide (CTAB), leading to CTAB modified γ-alumina nanoparticles (γANPs-CTAB). These novel functionalized γANPs-CTAB were characterized by XRPD, FTIR, and were used as an adsorbent for bisphenol-A (BPA) removal from water. Batch investigations were conducted under different experimental conditions (e.g., adsorbent dose, agitation time, initial concentration, and pH and surfactant loading) in order to optimize BPA adsorption and to identify the adsorption mechanisms in the system γANPs-CTAB-BPA. The effect of pH on the adsorption showed that the quantity of BPA removed increased remarkably until the pH value was 4, then remained almost constant until the pH value was up to 10, and then decreased for pH values greater than 10. For an initial BPA concentration of 20 mg/L and an adsorbent dose of 12.5 g/L at a pH value of 10, the removal efficiency achieved was 91.80 ± 0.21%. The adsorption mechanism was perfectly described by pseudo-second-order kinetics and the Langmuir isotherm. γANPs-CTAB materials were found to be effective adsorbents for BPA removal from water.

The arrangement of bisphenol A molecules into organoclays and their interactions with the intercalated surfactant were studied. The organoclays were prepared via solid-state intercalation of four cationic surfactants, such as dodecyltrimethyl-, tetradecyltrimethyl-, hexadecyltrimethyl-, and didodecyldimethyl-ammonium, as bromide salts, at different loading levels into the interlayers of two natural clays. The natural clays, the prepared organoclays, and the spent organoclays were characterized by X-ray powder diffraction, infrared spectroscopy, and scanning electron microscopy. X-ray powder diffraction measurements showed successive interlayer expansions of the d₀₀₁ basal spacing due to the intercalation of the cationic surfactants and the bisphenol A sorption. The increased d₀₀₁ basal spacing of the organoclays after bisphenol A sorption indicates that the molecules are integrated between the alkyl chains of the surfactant in the organoclays interlayers. Infrared spectroscopy was employed to probe the intercalation of the cationic surfactants and the sorbed bisphenol A. New characteristic bands attributed to the bisphenol A phenol rings appear in the range 1518–1613 cm⁻¹ on the infrared spectra of the spent organoclays, proving the presence of bisphenol A in the hydrophobic interlayers. Scanning electron microscopy of the organoclays before and after BPA sorption shows that their morphology becomes fluffy and that the presence of the organic molecules expands the clay structure.