The great increase in the production and consumption of plastics has resulted in large amounts of plastic wastes, creating a serious problem in terms of their environmentally friendly disposal. The need for the production of more environmentally friendly polymers gave birth to the production of biodegradable, and more recently, biobased polymers, used in the production of biodegradable or biobased plastics. Although the percentage of currently produced bioplastics is rather small, almost 1% compared to petrochemical-based plastics, inevitably is going to significantly increase in the near future due to strict legislation recently posed by the European Union and other countries’ Governments. Thus, recycling strategies that have been developed could be disturbed and the economic balance of this sector could be destabilized. In the present review, the recycling of the polymer mainly used in food plastic packaging, i.e., poly(ethylene terephthalate), PET is examined together with its counterparts from the biobased polymers, i.e., poly(lactic acid), PLA (already replacing PET in several applications), poly(3-hydroxybutyrate), PHB and poly(ethylene furanoate), PEF. Methods for the chemical recycling of these materials together with the chemical products obtained are critically reviewed. Specifically, hydrolysis, alcoholysis and glycolysis. Hydrolysis (i.e., the reaction with water) under different environments (alkaline, acidic, neutral), experimental conditions and catalysts results directly in the production of the corresponding monomers, which however, should be separated in order to be re-used for the re-production of the respective polymer. Reaction conditions need to be optimized with a view to depolymerize only a specific polymer, while the others remain intact. Alcoholysis (i.e., the reaction with some alcohol, methanol or ethanol) results in methyl or ethyl esters or diesters that again could be used for the re-production of the specific polymer or as a source for producing other materials. Glycolysis (reaction with some glycol, such as ethylene, or diethylene glycol) is much studied for PET, whereas less studied for the biopolymers and seems to be a very promising technique. Oligomers having two terminal hydroxyl groups are produced that can be further utilized as starting materials for other value-added products, such as unsaturated polyester resins, methacrylated crosslinked resins, biodegradable polyurethanes, etc. These diols derived from both PET and the bio-based polymers can be used simultaneously without the need for an additional separation step, in the synthesis of final products incorporating biodegradable units in their chemical structure.

The new trend in food packaging films is to use biodegradable or bio-based polymers, such as poly(lactic acid), PLA with additives such as thymol, carvacrol, limonene or cinnamaldehyde coming from natural resources (i.e., thyme, oregano, citrus fruits and cinnamon) in order to extent foodstuff shelf-life and improve consumers’ safety. Single, triple and quadruple blends of these active compounds in PLA were prepared and studied using the solvent-casting technique. The successful incorporation of the active ingredients into the polymer matrix was verified by FTIR spectroscopy. XRD and DSC data revealed that the crystallinity of PLA was not significantly affected. However, the Tg of the polymer decreased, verifying the plasticization effect of all additives. Multicomponent mixtures resulted in more intense plasticization. Cinnamaldehyde was found to play a catalytic role in the thermal degradation of PLA shifting curves to slightly lower temperatures. Release of thymol or carvacrol from the composites takes place at low rates at temperatures below 100 °C. A combined diffusion-model was found to simulate the experimental release profiles very well. Higher antioxidant activity was noticed when carvacrol was added, followed by thymol and then cinnamaldehyde and limonene. From the triple-component composites, higher antioxidant activity measured in the materials with thymol, carvacrol and cinnamaldehyde.

Multiwall carbon nanotubes (CNTs) and iron oxide impregnated carbon nanotubes (CNTs-iron oxide) were investigated for the adsorption of hazardous toluene and paraxylene (p-xylene) from aqueous solution. Pure CNTs were impregnated with iron oxides nanoparticles using wet impregnation technique. Various characterization techniques including thermogravimetric analysis, scanning electron microscopy, elemental dispersion spectroscopy, X-ray diffraction, and nitrogen adsorption analysis were used to study the thermal degradation, surface morphology, purity, and surface area of the materials. Batch adsorption experiments show that iron oxide impregnated CNTs have higher degree of removal of p-xylene (i.e., 90%) compared with toluene (i.e., 70%), for soaking time 2 h, with pollutant initial concentration 100 ppm, at pH 6 and shaking speed of 200 rpm at 25°C. Pseudo-second-order model provides better fitting for the toluene and p-xylene adsorption. Langmuir and Freundlich isotherm models demonstrate good fitting for the adsorption data of toluene and p-xylene.

Three types of LDPE‐based nanocomposites with montmorillonite clay, silica, and zinc oxide were prepared by melt blending the nanofiller with the resin. As a prelude to studying their durability, the extent of reinforcement of the LDPE matrix by the nanofillers was investigated using mechanical, thermal, and microscopic studies of the composites. No significant chemical modification of the polyethylene matrix was observed as a result of the processing of the composite compound. While reinforcement was obtained in all cases, the efficiency of reinforcement appears to be qualitatively influenced by surface functionalization, filler interactions, and the extent of dispersion of the filler in the matrix as well as the specific surface area of the nanoparticle fillers.